О1 1.2510 Блок СКС3

Контакты

Характеристики
O1 Tool Steel is the original oil-hardening, “non-shrinking” tool steel that can be hardened to the Rockwell C 65 range from a low austenitizing temperature. O1 is a general-purpose tool steel that is typically used in applications where alloy steels cannot provide sufficient hardness, strength, and wear resistance.

ПРИЛОЖЕНИЯ: Если требуется более высокая стабильность размеров при термообработке или повышенная износостойкость, следует рассмотреть инструментальные стали с более высоким содержанием легирующих элементов, такие как A2 или D2.

СОСТАВ

C

Mn

Si

Cr

W

0.94

1.20

0.30

0.50

0.50

СООТВЕТСТВЕННЫЕ СВОЙСТВА

1492433770224674

Коэффициент теплового расширения (63-64HRC)

Температура︒F

дюйм/дюйм︒F×10-6

Температура︒С

мм/мм︒C×10-6

100-500

5.96

38-260

10.73

100-800

7.14

38-427

12.85

100-1000

7.84

38-538

14.11

100-1200

8.02

38-649

14.44

ФИЗИЧЕСКИЕ СВОЙСТВА

· Плотность: 0.283 фунта/дюйм3 (7833 кг/м3)

· Удельный вес: 7.83

· Модуль упругости: 31 x 106 фунтов на квадратный дюйм (214 ГПа)

· Обрабатываемость: 85-90% 1% углеродистой стали.

1492433836447736

Heat Treatment Response

Air Cooled from

HRC

1425F(774︒C),30 minutes

62

1450F(788︒C),30 minutes

64

1475F(802︒C),30 minutes

65

1500F(816︒C),30 minutes

65

1600F(871︒C),30 minutes

64

ИНСТРУКЦИЯ ПО ТЕРМООБРАБОТКЕ

ЗАКАЛКА

КРИТИЧЕСКАЯ ТЕМПЕРАТУРА:

Ac1: 1350°F(732℃)

Ac3: 1440°F(760℃)

AR1: 1295°F(703℃)

AR3: 1240°F(671℃)

Предварительный нагрев: Heat at a rate not exceeding 400°F per hour (222°C per hour) to 1200-1300°F (649-704°C) and equalize.

Austenitizing (High Heat): Heat slowly from the preheat to 1475-1500°F (802-816C)

Soak for 30 minutes for the first inch (25.4 mm) of thickness, plus 15 minutes for each additional inch (25.4 mm).

Закалка: Oil quench to a temperature no lower than 150-125°F (66-51°C).

Note: O1 is somewhat prone to quench cracking, especially if there are significant changes in section thickness and sharp internal corners. The oil quenching should be performed so that the heat removal is as uniform as possible in all areas of the part being quenched. Be sure to remove the part from the oil before the temperature drops to ambient temperature. Hot oil at a temperature of 300 to 400°F (149-204°C) is recommended.

Темперирование: Temper immediately after quenching. Do not allow the part to cool below 125°F (51°C). The typical tempering range is 350 - 400°F (177 -204°C). Hold at temperature for 1 hour per inch (25.4 mm) of thickness, 2 hours minimum, then air cool to ambient temperature. To minimize internal stresses in cross sections greater than 3 inches (76.2 mm) and to improve stability in parts that will be EDM’d after heat treatment, a soaking time of 4 to 6 hours at the tempering temperature is strongly recommended.

Cryogenic Treatment: Refrigeration treatments should typically be performed after the temper, and must be followed by a second temper.

ОТЖИГ

Отжиг необходимо проводить после горячей обработки и перед повторной закалкой.

Heat at a rate not exceeding 400°F per hour (222°C per hour) to 1425 -1450°F (802-816°C), and hold at temperature for 1 hour per inch (25.4mm) of maximum thickness; 2 hours minimum. Then cool slowly with the furnace at a rate not exceeding 50°F per hour (28°C per hour) to 1000°F (538°C). Continue cooling to ambient temperature in the furnace or in air. The resultant hardness should be a maximum of 212 HBW.

НаименованияРазмер (мм)ОбработкаУсловия доставки
Круглый стерженьДИАМ1.0 - 30Холодное волочение / Бесцентровое шлифованиеЯркий и отжиг
ДИАМ20 - 80ПилингЯркий и отжиг
ДИА 13-180ГорячекатаныйЧерная поверхность и отжиг
ДИАМ 70 - 400ГорячекатаныйЧерная поверхность и отжиг
Плоский барТ 3.0-20 ХВ 20-100ГорячекатаныйЧерная поверхность и отжиг
ЗаблокироватьТ 20-200 Х 300-800Горячекатаный и горячекованыйЧерная поверхность/Машина и отжиг
КатанкаДИАМ 5.5 - 13ГорячекатаныйЧерная поверхность и отжиг
ЛистыT1.0 - 2.5ХолоднокатаныеЧерная поверхность и отжиг
Т 2.5 - 8.0ГорячекатаныйЧерная поверхность и отжиг
Связаться с нами

Горячие категории