О1 1.2510 СКС3

Главная>Наша продукция >Инструментальная сталь для холодной обработки>О1 1.2510 СКС3

Cold Working Tool Steel O1 1.2510 SKS3 sheets

Контакты

Характеристики

O1 tool steel is a low alloy cold work tool steel that must be oil-quenched in heat treatment. O1 tool steel contains small amounts of manganese, tungsten, and chromium, giving O1 tool steel adequate toughness for normal tool & die uses. O1 tool steel has deep hardening properties with fine grain structure with unusual toughness. O1 tool steel has good response to heat treatment with small dimensional changes. Sizes over approximately 2 inches thick or round may exhibit a lower hardness in the interior. O1 tool steel is available in standard de-carb free rounds, flats and squares, as well as the largest size selection in ground flat stock and drill rod of all the tool steel grades.


Области применения:

Where greater dimensional stability in heat treatment or improved wear resistance is required, tool steels with higher alloy contents, such as A2 or D2 should be considered.


СОСТАВ

CMnSi
Cr
W
0.94
1.200.300.50
0.50


Технические характеристики:

ASTM O1 Tool Steel Mechanical Properties

ОбъектыМетрикаимператорский
Hardness, Brinell (soft annealed -delivery condition)190190
Hardness, Rockwell C (tempering temp 300-1200°F)34.0-64.034.0-64.0
Elastic modulus (hardened to 62 HRC)193 ГПа28000 KSI
Elastic modulus (@399°C/750°F, hardened to 62 HRC )172 ГПа25000 KSI
Elastic modulus (@191°C/375°F, hardened to 62 HRC)186 ГПа27000 KSI
Compressive yield strength (0.2%, hardened to 50 HRC)1350 МПа196000 PSI
Compressive yield strength (0.2%, hardened to 55 HRC)1800 МПа261000 PSI
Compressive yield strength (0.2%, hardened to 60 HRC)2150 МПа312000 PSI
Compressive yield strength (0.2%, hardened to 62 HRC)2200 МПа319000 PSI


Физические свойства

ОбъектыМетрикаимператорский
Плотность (закалка до 62 HRC)7.81 г / cm30.282 фунта / дюйм3
Density (@399°C/ 750°F, hardened to 62 HRC)7.70 г / cm30.278 фунта / дюйм3
Density (@191°C/ 375°F, hardened to 62 HRC)7.75 г / cm30.280 фунта / дюйм3
Температура плавления1421 ° C2590 ° F


Тепловые свойства

ОбъектыConditions
Т (° С)Лечение
Термическое расширение10.6 x 10-6 / ºC20-260


Forging of ASTM O1 Tool Steel

Heating for forging of oil tool steel O1 must be done slowly and uniformly. Forging of alloy O1 steels can be performed at 980-1000°C, and reheat as often as necessary. But not forge below 800°C. After forging AISI O1 tool steel, cool slowly in lime, mica, dry ashes or furnace. ASTM O-1 tool steels should always be annealed after forging.


AISI O1 Tool Steel Heat Treatment


Anneal

Отжиг необходимо проводить после горячей обработки и перед повторной закалкой.

Heat at a rate not exceeding 222°C per hour to 802-816°C, and hold at temperature for 1 hour per inch (25.4mm) of maximum thickness; 2 hours minimum. Then cool slowly with the furnace at a rate not exceeding 28°C per hourto 538°C. Continue cooling to ambient temperature in the furnace or in air. The resultant hardness should be a maximum of 212 HBW.


Stress Relief of Unhardened Material

Heat slowly to 1250° F. Soak for two hours per inch of thickness at heat. Slow cool (furnace cool if possible) to room temperature.


Hardening

1.Preheat: Warm slightly before charging into the preheat furnace, which should be operating at about 1100°-1200°F.

2.Hardening: Heat to 1475 to 1500° F. Soak at heat for 30 minutes per inch of thickness.

3.Quench: Quench O1 steel in warm oil and allow to cool in the oil until a temperature of 125°-150°F has been reached, or to where the part can be held in the bare hand, and temper immediately.

4.Temper: Normally oil hardening steels need to be single tempered only. However, double tempering may sometimes be preferred. Soak at heat for 2 hours per inch of thickness for each temper. Air cool to room temperature between tempers. The normal tempering range for this grade is 300 to 450° F.


 Stress Relief Temper

A stress relief temper for hardened material is strongly recommended after significant grinding, or welding, or EDM. Select a temperature that is 25 or 50° F lower than the last tempering temperature used.


 НаименованияDimension  (mm)ОбработкаУсловия доставки
ЛистыT1.0 - 2.5ХолоднокатаныеЧерная поверхность и отжиг
Т 2.5 - 8.0ГорячекатаныйЧерная поверхность и отжиг