HSS M42 round bar

Контакты

Характеристики

High-speed steel M42 steel is widely used in metal manufacturing industries and in cutting tools manufacturing because of its superior red-hardness as compared to more conventional high-speed steels, allowing for shorter cycle times in production environments due to higher cutting speeds or from the increase in time between tool changes. HSS M42 tool steel is also less prone to chipping when used for interrupted cuts and costs less when compared to the same tool made of carbide. Tools made from cobalt-bearing high speed steels can often be identified by the letters HSS-Co.

AISI M42 tool steel is a conventionally manufactured cobalt alloyed high-speed steel. The various stages of the manufacturing process are chosen and controlled so that an end product is obtained with a good structure in terms of carbide size and distribution. This is a distinct advantage for the finished tool.


Области применения:Twist drills, taps, milling cutters, reamers, broaches, saws, knives, and thread rolling dies.


Описание: M42 ROUND BAR 


СОСТАВ        

        C       Si       Cr
       W
       Mo
        V 
      Co
     1.08
     0.45     3.85
     1.50
      9.50
      1.20
     8.00


СООТВЕТСТВЕННЫЕ СВОЙСТВА

ФИЗИЧЕСКИЕ СВОЙСТВА

· Плотность: 0.282 фунта/дюйм3 (7806 кг/м3)

· Удельный вес: 7.81

· Modulus of Elasticity: 30 x 106 psi (207 GPa)

· Обрабатываемость: 35-40% 1% углеродистой стали.


HEAT TREATING INSTRUCTIONS: HARDENING

ЗАКАЛКА
КРИТИЧЕСКАЯ ТЕМПЕРАТУРА:
Ac1: 1560°F(849℃)


Machinability

M42 tool steel can be drilled, turned, threaded, broached, milled and tapped when it is in its annealed condition and rated at 45% of 1% carbon steel.


Ковка

M42 molybdenum high speed tool steel is preheated to 871°C (1599°F) in a slow manner and then soaked. This is followed by rapid heating to 1093°C (1999°F) and slow cooling. Temperatures below 982°C (1799°F) are not suitable for the forging process.


закал

M42 tool steel is tempered for three times at 538-593°C (1000-1099°F) and then cooled completely between cycles to obtain good results. Tempering is performed in vacuum furnaces or in salt baths.


отжиг

M42 tool steel is heated at 871°C (1599°F) and then cooled slowly in a furnace.


Закаливание

M42 tool steel is preheated to 871°C (1599°F), soaked and finally heated to 1204°C (2199°F).


гашение

A salt media is used for quenching M42 tool steel at 538°C (1000°F) and then the steel is air cooled.


НаименованияРазмеры (мм)ОбработкаУсловия доставки


Круглый стержень

ДИАМ1.0 - 30Холодное волочение / Бесцентровое шлифованиеЯркий и отжиг
ДИАМ20 - 80ПилингЯркий и отжиг
ДИА 13-180ГорячекатаныйЧерная поверхность и отжиг
ДИАМ 70 - 400ГорячекатаныйЧерная поверхность и отжиг