Д3 1.2080 СКД1

Главная>Наша продукция >Инструментальная сталь для холодной обработки>Д3 1.2080 СКД1

Катанка Д3 1.2080 СКД1

Контакты

Характеристики
D3 Tool Steel is a high-carbon, high-chromium, oil-hardening tool steel that is characterized by a relatively high attainable hardness and numerous, large, chromium-rich alloy carbides in the microstructure. These carbides provide good resistance to wear from sliding contact with other metals and abrasive materials.

D3 exhibits excellent stability in heat treatment, holding size almost as well as the air-hardening, high-carbon, high-chromium die steels such as D2.

ПРИЛОЖЕНИЯ: Формовочные валки, волочильные штампы, формовочные инструменты, инструменты для уплотнения порошков и штампы для ламинирования.

СОСТАВ

C

Mn

Si

Cr

V

2.15

0.40

0.40

12.25

0.25

СООТВЕТСТВЕННЫЕ СВОЙСТВА

1492432113498899

Коэффициент теплового расширения (58-59HRC)

Температура︒F

in/in︒F×10-6

Температура︒С

mm/mm︒C×10-6

100-500

6.58

38-260

11.84

100-800

7.15

38-427

12.87

100-1000

7.32

38-538

13.81

100-1200

7.54

38-649

13.57

100-1500

7.72

38-816

13.90

ФИЗИЧЕСКИЕ СВОЙСТВА

· Density: 0.284 lb/in3 (7870 kg/m3)

· Specific Gravity: 7.87

· Modulus of Elasticity: 30 x 106 psi (207GPa)

· Electrical Resistivity: 54.8 uOhm-cm at 70ºF (21ºC)

· Machinability: 45-50% of a 1% carbon steel

1492432147401951

ИНСТРУКЦИЯ ПО ТЕРМООБРАБОТКЕ

ЗАКАЛКА

КРИТИЧЕСКАЯ ТЕМПЕРАТУРА:

Ac1: 1440°F(782℃)

Ac3: 1530°F(8320℃)

AR1: 1410°F(766℃)

AR3: 1370°F(743℃)

Предварительный нагрев: To minimize distortion and stresses in large or complex tools use a double preheat. Heat at a rate not exceeding 400°F per hour (222°C per hour) to 1200-1250°F (649-677°C) equalize, then heat to 1400-1450°F (760-788°C). For normal tools, use only the first temperature range as a single preheating treatment.

Austenitizing (High Heat): Heat slowly from the preheat to 1700-1750°F (927-954°C)

Quenching: For oil, quench until black, about 900°F (482°C), then cool in still air to 150-125°F (66-51°C).

For pressurized gas, the furnace should have a minimum quench pressure of 4 bars. A quench rate of approximately 400°F (222°C) per minute to below 1000°F (538°C) is critical to obtain the desired properties.

Темперирование: Temper immediately after quenching. Hold at temperature for 1 hour per inch (25.4 mm) of thickness, 2 hours minimum, then air cool to ambient temperature.

For maximum wear resistance, temper between 300-350°F (149-177°C) for a hardness of 62-63 HRC. For the optimal balance between wear resistance and toughness, temper between 450-500°F (232-260°C). This will produce 58-60 HRC.

To minimize internal stresses in cross sections greater than 6 inches (152.4 mm) and to improve stability in tools that will be EDM'd after heat treatment, soaking times of 4 to 6 hours at the tempering temperature are strongly recommended.

ОТЖИГ

Отжиг необходимо проводить после горячей обработки и перед повторной закалкой.

Нагревайте со скоростью, не превышающей 400°F в час (222°C в час), до 1600–1650°F (871–899°C) и выдерживайте при температуре 1 час на дюйм (25.4 мм) максимальной толщины; 2 часа минимум. Затем медленно охладите в печи со скоростью, не превышающей 50°F в час (28°C в час) до 1000°F (538°C). Продолжайте охлаждение до температуры окружающей среды в печи или на воздухе. Результирующая твердость должна составлять максимум 255 HBW.

Cryogenic Treatment: Refrigeration treatments should typically be performed after the first temper, and must be followed by a second temper


НаименованияРазмер (мм)ОбработкаУсловия доставки
Круглый стерженьДИАМ1.0 - 30Холодное волочение / Бесцентровое шлифованиеЯркий и отжиг
ДИАМ20 - 80ПилингЯркий и отжиг
ДИА 13-180ГорячекатаныйЧерная поверхность и отжиг
ДИАМ 70 - 400ГорячекатаныйЧерная поверхность и отжиг
Плоский барТ 3.0-20 ХВ 20-100ГорячекатаныйЧерная поверхность и отжиг
ЗаблокироватьТ 20-200 Х 300-800Горячекатаный и горячекованыйЧерная поверхность/Машина и отжиг
КатанкаДИАМ 5.5 - 13ГорячекатаныйЧерная поверхность и отжиг
ЛистыT1.0 - 2.5ХолоднокатаныеЧерная поверхность и отжиг
Т 2.5 - 8.0ГорячекатаныйЧерная поверхность и отжиг