Cold Working Tool Steel D3 1.2080 SKD1 sheets

Контакты

Характеристики

AISI D3 alloy steel is heat treatable and will offer a hardness in the range 58-64 HRC. After heat treatment D3 tool steel is hard, durable and dense, and is immune from sinking in use. It offers a measure of corrosion resistance when polished. In general, the applications of AISI D3 tool steel resemble those of D2 tool steel but it should be remembered that alloy tool steel D3 has better wear resistance of the two steels and is preferred for such items as shear blades. Owing to its higher wear resistance, AISI / ASTM D3 cold work steel is slightly more difficult to grind than D2 steels.


Области применения:

D3 tool steel used for cold work tool products. Like forming dies , thread rolling dies, cutting knife, etc.


СОСТАВ

C
MnSiCrV
2.15
0.400.40
12.250.25


Технические характеристики:

D3 Steel sheets: thickness 10 –500mm x width 200– 1400mm


Chemical Composition of D3 Tool Steel Material

ASTM A681CSiMnPSCrMoV
D3/T304021.40 ~ 1.600.10 ~ 0.600.20 ~ 0.600.030 Макс. 0.030 Макс.11.0 ~ 13.00.70 ~ 1.200.50 ~ 1.10
DIN 17350CSiMnPSCrMoV
1.2080/С210Кр12 1.50 ~ 1.600.10 ~ 0.400.15 ~ 0.450.030 Макс.0.030 Макс.        11.0 ~ 12.00.60 ~ 0.800.90 ~ 1.10
GB / T 1299CSi
MnP
SCrMoV
Cr121.40 ~ 1.60≤0.60≤0.600.030 Макс.        0.030 Макс.11.00 ~ 13.000.70 ~ 1.20≤1.10
JIS G4404CSiMnPSCrMoV
SKD11.40 ~ 1.60≤0.40≤0.600.030 Макс.0.030 Макс.        11.0 ~ 13.00.80 ~ 1.200.20 ~ 0.50

D3 tool Steel Equivalent and Related Specification

СШАНемецкийЯпонияКитайISO
ASTM A681DIN 17350JIS G4404GB / T 1299ISO 4957
D31.2080SKD1Cr12X200Cr12


ASTM AISI D3 Tool Steel Material Mechanical Properties

Hardness, Rockwell C: 63 HRC

Izod impact unnotched: 77 J.


Forged of hot work D3 Steel material metal

Forged D3 tool steel at 954 – 1065 ºC. no forging when below 926 ºC.


Heat Treatment of SAE/AISI D3Steel

D3 Steel Annealing

Slowly heat to 871-898 ºC, keep enough time, then cooling in furnace at 4-5 ºC per hour.


D3 tool Steel Hardening & Quenching

Температура закалки / ℃ | печь для соляной ванны: 954

Температура закалки / ℃ | печь с контролируемой атмосферой: 968

The heat preservation time/min: 10 to 20

Quenching medium: oil


Tempering Of D3 Steel

Температура отпуска / ℃: 204

После отпуска твердость HRC или выше: 61.


НаименованияРазмер (мм)ОбработкаУсловия доставки
Листы        T1.0 - 2.5ХолоднокатаныеЧерная поверхность и отжиг
Т 2.5 - 8.0ГорячекатаныйЧерная поверхность и отжиг