M42

Acasă>Produse>Oțel de mare viteză>M42

HSS M42 round bar

Contact

Specificații

High-speed steel M42 steel is widely used in metal manufacturing industries and in cutting tools manufacturing because of its superior red-hardness as compared to more conventional high-speed steels, allowing for shorter cycle times in production environments due to higher cutting speeds or from the increase in time between tool changes. HSS M42 tool steel is also less prone to chipping when used for interrupted cuts and costs less when compared to the same tool made of carbide. Tools made from cobalt-bearing high speed steels can often be identified by the letters HSS-Co.

AISI M42 tool steel is a conventionally manufactured cobalt alloyed high-speed steel. The various stages of the manufacturing process are chosen and controlled so that an end product is obtained with a good structure in terms of carbide size and distribution. This is a distinct advantage for the finished tool.


Aplicații:Twist drills, taps, milling cutters, reamers, broaches, saws, knives, and thread rolling dies.


Detaliu rapid: M42 ROUND BAR 


COMPOZIȚIE        

        C       Si       Cr
       W
       Mo
        V 
      Co
     1.08
     0.45     3.85
     1.50
      9.50
      1.20
     8.00


PROPRIETĂȚI RELATIVE

PROPRIETĂȚI FIZICE

· Densitate: 0.282 lb/in3 (7806 kg/m3)

· Greutate specifică: 7.81

· Modulul de elasticitate: 30 x 106 psi (207 GPa)

· Prelucrabilitate: 35-40% dintr-un oțel carbon de 1%.


INSTRUCȚIUNI DE TRATARE TERMICA: CĂLIRE

CALITIRE
TEMPERATURA CRITICA:
Ac1: 1560°F (849°C)


Prelucrabilitate

M42 tool steel can be drilled, turned, threaded, broached, milled and tapped when it is in its annealed condition and rated at 45% of 1% carbon steel.


Forjare

M42 molybdenum high speed tool steel is preheated to 871°C (1599°F) in a slow manner and then soaked. This is followed by rapid heating to 1093°C (1999°F) and slow cooling. Temperatures below 982°C (1799°F) are not suitable for the forging process.


Calirea

M42 tool steel is tempered for three times at 538-593°C (1000-1099°F) and then cooled completely between cycles to obtain good results. Tempering is performed in vacuum furnaces or in salt baths.


Recoacerea

M42 tool steel is heated at 871°C (1599°F) and then cooled slowly in a furnace.


călire

M42 tool steel is preheated to 871°C (1599°F), soaked and finally heated to 1204°C (2199°F).


Stingerea

A salt media is used for quenching M42 tool steel at 538°C (1000°F) and then the steel is air cooled.


ArticolDimensiuni (mm)ProcesConditii de livrare


Barul rotund

DIA1.0 - 30Desen la rece / rectificare fără centruBright & Anneal
DIA20 - 80CoajăBright & Anneal
DIA 13-180Laminate la caldSuprafață neagră și recuit
DIA 70 - 400Laminate la caldSuprafață neagră și recuit