H13 1.2344 SKD61

Acasă>Produse>Oțeluri pentru unelte de lucru la cald>H13 1.2344 SKD61

H13 1.2344 SKD61 flat bar

Contact

Specificații

H13 Tool Steel is a versatile chromium-molybdenum hot work steel that is widely used in hot work and cold work tooling applications. The hot hardness (hot strength) of H13 resists thermal fatigue cracking which occurs as a result of cyclic heating and cooling cycles in hot work tooling applications. Because of its excellent combination of high toughness and resistance to thermal fatigue cracking (also known as heat checking) H13 is used for more hot work tooling applications than any other tool steel.

Because of its high toughness and very good stability in heat treatment, H13 is also used in a variety of cold work tooling applications. In these applications, H13 provides better hardenability (through hardening in large section thicknesses) and better wear resistance than common alloy steels such as 4140.

Also available as Electro-Slag-Remelted (ESR) and Vacuum-Arc-Remelted (VAR) products as well. The remelting processes provide improved chemical homogeneity, refinement of carbide size, and the associated improvements in mechanical properties and fatigue properties.

APLICATII:Inserts, cores, and cavities for die casting dies, die casting shot sleeves, hot forging dies, extrusion dies, and plastic mold cavities and components that require high toughness and excellent polishability.

COMPOZIȚIE

C

Mn

Si

Cr

Mo

V

0.40

0.40

1.00

5.25

1.35

1.00


Conductivitate termică

Temperatura︒F

Btu/hr-ft︒F

Temperatura︒C

W/m︒C

80

10.17

27

17.6

400

13.52

204

23.4

800

14.5

427

25.1

1200

15.49

649

26.8

PROPRIETĂȚI FIZICE

· Densitate: 0.280 lb/in3 (7750 kg/m3)

· Greutate specifică: 7.75

· Prelucrabilitate: 65-70% dintr-un oțel carbon de 1%.

Modul de elasticitate

Temp︒F

Modulus psi×10-6

Temp︒C

Modulus Gpa

70

30.0

21

206.8

200

29.0

93

199.9

400

27.0

204

186.2

600

28.5

316

196.5

800

27.5

427

189.6

1000

23.0

538

158.6

 

Coeficientul de dilatare termică (47-48 HRC)

Temperatura︒F

in/in︒F×10-6

Temperatura︒C

mm/mm︒C×10-6

80-200

5.8

21-93

10.4

80-400

6.3

21-204

11.3

80-800

6.9

21-316

12.4

80-1200

7.3

21-427

13.1

80-1500

7.5

21-538

13.


1492431268787984


INSTRUCȚIUNI DE TRATARE TERMICA

CALITIRE

TEMPERATURA CRITICA:

Ac1: 1544°F (840°C)

Ac3: 1634°F (890°C)

AR1: 1475 ° F (802 ℃)

AR3: 1418 ° F (826 ℃)

Preîncălzire: To minimize distortion in complex tools use a double preheat. Heat at a rate not exceeding 400°F per hour (222°C per hour) to 1150-1250°F (621-677°C), equalize, then raise to 1500-1600°F (816-871°C) and equalize. For normal tools, use only the second temperature range as a single preheating treatment.

Austenitizing (High Heat): Heat rapidly from the preheat. Furnace or Salt: 1800-1890°F (982-1032°C) For maximum toughness, use 1800°F (982°C) For maximum hardness and resistance to thermal fatigue cracking and wear use 1890 (1032°C). Soak at temperature for 30 to 90 minutes.

Stingerea: Air, pressurized gas, or warm oil. Section thicknesses up to and including 5 inches (127 mm) will typically fully through harden when cooled in still air from the austenitizing treatment. Sections greater than 5 inches (127 mm) in thickness will require accelerated cooling by using forced air, pressurized gas, or an interrupted oil quench to obtain maximum hardness, toughness and resistance to thermal fatigue cracking.

For pressurized gas quenching, a minimum quench rate of approximately 50°F per minute (28°C per minute) to below 1000°F (538°C) is required to obtain the optimum properties in the steel.

For oil, quench until black, about 900°F (482°C), then cool in still air to 150-125°F (66-51°C).

Temperare: Temper immediately after quenching. The typical tempering range is 1000-1150°F (538-621°C). Hold at the tempering temperature for 1 hour per inch (25.4mm) of thickness, but for 2 hours minimum, then air cool to ambient temperature. Double tempering is required. To maximize toughness and tool performance, a third temper is often used as a stress relief after all finish machining, grinding, and EDM work are completed on the tool.

recoacerea în

Recoacerea trebuie efectuată după prelucrarea la cald și înainte de reîntărire.

Heat at a rate not exceeding 400°F per hour (222°C per hour) to 1575-1625°F (857-885°C), and hold at temperature for 1 hour per inch of maximum thickness; 2 hours minimum. Then cool slowly with the furnace at a rate not exceeding 50°F per hour (28°C per hour) to 1000°F (538°C). Continue cooling to ambient temperature in the furnace or in air. The resultant hardness should be a maximum of235 HBS.


ArticolDimensiune (mm)ProcesConditii de livrare
Barul rotundDIA1.0 - 30Desen la rece / rectificare fără centruBright & Anneal
DIA20 - 80CoajăBright & Anneal
DIA 13-180Laminate la caldSuprafață neagră și recuit
DIA 70 - 400Laminate la caldSuprafață neagră și recuit
Bar platT 3.0-20 XW 20-100Laminate la caldSuprafață neagră și recuit
BlocaT 20-200 X 300-800Laminat la cald și forjat la caldSuprafață neagră / Machine & Anneal
SârmăDIA 5.5 - 13Laminate la caldSuprafață neagră și recuit
AsternuturiT1.0 - 2.5Laminate la receSuprafață neagră și recuit
T 2.5 - 8.0Laminate la caldSuprafață neagră și recuit