D3 1.2080 SKD1

Acasă>Produse>Oțel pentru scule de lucru la rece>D3 1.2080 SKD1

D3 1.2080 SKD1 tijă

Contact

Specificații
D3 Tool Steel is a high-carbon, high-chromium, oil-hardening tool steel that is characterized by a relatively high attainable hardness and numerous, large, chromium-rich alloy carbides in the microstructure. These carbides provide good resistance to wear from sliding contact with other metals and abrasive materials.

D3 exhibits excellent stability in heat treatment, holding size almost as well as the air-hardening, high-carbon, high-chromium die steels such as D2.

APLICATII: Role de formare, matrițe de tragere, scule de formare, compactare a pulberii și matrițe de laminare.

COMPOZIȚIE

C

Mn

Si

Cr

V

2.15

0.40

0.40

12.25

0.25

PROPRIETĂȚI RELATIVE

1492432113498899

Coeficientul de dilatare termică (58-59 HRC)

Temperatura︒F

in/in︒F×10-6

Temperatura︒C

mm/mm︒C×10-6

100-500

6.58

38-260

11.84

100-800

7.15

38-427

12.87

100-1000

7.32

38-538

13.81

100-1200

7.54

38-649

13.57

100-1500

7.72

38-816

13.90

PROPRIETĂȚI FIZICE

· Densitate: 0.284 lb/in3 (7870 kg/m3)

· Greutate specifică: 7.87

· Modulul de elasticitate: 30 x 106 psi (207GPa)

· Electrical Resistivity: 54.8 uOhm-cm at 70ºF (21ºC)

· Prelucrabilitate: 45-50% dintr-un oțel carbon de 1%.

1492432147401951

INSTRUCȚIUNI DE TRATARE TERMICA

CALITIRE

TEMPERATURA CRITICA:

Ac1: 1440°F (782°C)

Ac3: 1530°F (8320°C)

AR1: 1410 ° F (766 ℃)

AR3: 1370 ° F (743 ℃)

Preîncălzire: To minimize distortion and stresses in large or complex tools use a double preheat. Heat at a rate not exceeding 400°F per hour (222°C per hour) to 1200-1250°F (649-677°C) equalize, then heat to 1400-1450°F (760-788°C). For normal tools, use only the first temperature range as a single preheating treatment.

Austenitizing (High Heat): Heat slowly from the preheat to 1700-1750°F (927-954°C)

Quenching: For oil, quench until black, about 900°F (482°C), then cool in still air to 150-125°F (66-51°C).

For pressurized gas, the furnace should have a minimum quench pressure of 4 bars. A quench rate of approximately 400°F (222°C) per minute to below 1000°F (538°C) is critical to obtain the desired properties.

Temperare: Temper immediately after quenching. Hold at temperature for 1 hour per inch (25.4 mm) of thickness, 2 hours minimum, then air cool to ambient temperature.

Pentru rezistență maximă la uzură, temperați între 300-350°F (149-177°C) pentru o duritate de 62-63 HRC. Pentru echilibrul optim între rezistența la uzură și duritate, temperați între 450-500°F (232-260°C). Aceasta va produce 58-60 HRC.

To minimize internal stresses in cross sections greater than 6 inches (152.4 mm) and to improve stability in tools that will be EDM'd after heat treatment, soaking times of 4 to 6 hours at the tempering temperature are strongly recommended.

recoacerea în

Recoacerea trebuie efectuată după prelucrarea la cald și înainte de reîntărire.

Încălziți la o viteză care nu depășește 400°F pe oră (222°C pe oră) la 1600-1650°F (871-899°C) și mențineți la temperatură timp de 1 oră pe inch (25.4 mm) de grosime maximă; 2 ore minim. Apoi se răcește lent cu cuptorul la o viteză care nu depășește 50°F pe oră (28°C pe oră) până la 1000°F (538°C). Continuați să răciți la temperatura ambiantă în cuptor sau în aer. Duritatea rezultată ar trebui să fie de maximum 255 HBW.

Cryogenic Treatment: Refrigeration treatments should typically be performed after the first temper, and must be followed by a second temper


ArticolDimensiune (mm)ProcesConditii de livrare
Barul rotundDIA1.0 - 30Desen la rece / rectificare fără centruBright & Anneal
DIA20 - 80CoajăBright & Anneal
DIA 13-180Laminate la caldSuprafață neagră și recuit
DIA 70 - 400Laminate la caldSuprafață neagră și recuit
Bar platT 3.0-20 XW 20-100Laminate la caldSuprafață neagră și recuit
BlocaT 20-200 X 300-800Laminat la cald și forjat la caldSuprafață neagră / Machine & Anneal
SârmăDIA 5.5 - 13Laminate la caldSuprafață neagră și recuit
AsternuturiT1.0 - 2.5Laminate la receSuprafață neagră și recuit
T 2.5 - 8.0Laminate la caldSuprafață neagră și recuit