D3 1.2080 SKD1

Acasă>Produse>Oțel pentru scule de lucru la rece>D3 1.2080 SKD1

Table de oțel pentru scule de lucru la rece D3 1.2080 SKD1

Contact

Specificații

AISI D3 alloy steel is heat treatable and will offer a hardness in the range 58-64 HRC. After heat treatment D3 tool steel is hard, durable and dense, and is immune from sinking in use. It offers a measure of corrosion resistance when polished. In general, the applications of AISI D3 tool steel resemble those of D2 tool steel but it should be remembered that alloy tool steel D3 has better wear resistance of the two steels and is preferred for such items as shear blades. Owing to its higher wear resistance, AISI / ASTM D3 cold work steel is slightly more difficult to grind than D2 steels.


Aplicații:

D3 tool steel used for cold work tool products. Like forming dies , thread rolling dies, cutting knife, etc.


COMPOZIȚIE

C
MnSiCrV
2.15
0.400.40
12.250.25


Specificații:

D3 Steel sheets: thickness 10 –500mm x width 200– 1400mm


Chemical Composition of D3 Tool Steel Material

ASTM A681CSiMnPSCrMoV
D3/T304021.40 ~ 1.600.10 ~ 0.600.20 ~ 0.600.030 Max 0.030 Max11.0 ~ 13.00.70 ~ 1.200.50 ~ 1.10
DIN 17350CSiMnPSCrMoV
1.2080/X210Cr12 1.50 ~ 1.600.10 ~ 0.400.15 ~ 0.450.030 Max0.030 Max        11.0 ~ 12.00.60 ~ 0.800.90 ~ 1.10
GB / T 1299CSi
MnP
SCrMoV
Cr121.40 ~ 1.60≤ 0.60≤ 0.600.030 Max        0.030 Max11.00 ~ 13.000.70 ~ 1.20≤ 1.10
JIS G4404CSiMnPSCrMoV
SKD11.40 ~ 1.60≤ 0.40≤ 0.600.030 Max0.030 Max        11.0 ~ 13.00.80 ~ 1.200.20 ~ 0.50

D3 tool Steel Equivalent and Related Specification

Statele Unite ale AmericiiGermanăJaponiaChinaISO
ASTM A681DIN 17350JIS G4404GB / T 1299ISO 4957
D31.2080SKD1Cr12X200Cr12


ASTM AISI D3 Tool Steel Material Mechanical Properties

Hardness, Rockwell C: 63 HRC

Izod impact unnotched: 77 J.


Forged of hot work D3 Steel material metal

Forged D3 tool steel at 954 – 1065 ºC. no forging when below 926 ºC.


Heat Treatment of SAE/AISI D3Steel

D3 Steel Annealing

Slowly heat to 871-898 ºC, keep enough time, then cooling in furnace at 4-5 ºC per hour.


D3 tool Steel Hardening & Quenching

Temperatura de stingere / ℃ | cuptor cu baie de sare: 954

Temperatura de stingere / ℃ | cuptor cu atmosferă controlată: 968

The heat preservation time/min: 10 to 20

Quenching medium: oil


Tempering Of D3 Steel

Temperatura de temperare / ℃ : 204

După revenire duritate HRC sau mai mare: 61


ArticolDimensiune (mm)ProcesConditii de livrare
Asternuturi        T1.0 - 2.5Laminate la receSuprafață neagră și recuit
T 2.5 - 8.0Laminate la caldSuprafață neagră și recuit