O1 1.2510 SKS3

Início>Produtos>Aço ferramenta para trabalho a frio>O1 1.2510 SKS3

Bloco de aço ferramenta para trabalho a frio O1 1.2510 SKS3

Fale conosco

Especificações

O1 tool steel is an oil hardening, cold work general purpose steel with easy machining properties and low hardening temperatures compared to other grades. O1 provides good wear resistance and toughness sufficient for standard tool and die applications making it a suitable choice for tooling with good tool life and economical production. In situations that require greater size stability during hardening, A2 should be considered. Some common applications include: bending dies, trimmer dies, perforators, broaches, blanking dies, forming dies, cutting dies, bushings, forming rolls, knives, drawing dies, and embossing dies. O1 plates and flats are supplied in a decarb free and annealed condition.


Aplicações:

1.Used for make cold die with small cross section and complicated shape and high precision

2. Used to make sheet stamping touch, jewelry embossing mold

3. Widely used in cutting tools, such as broaches, filament taps, long reamer, special milling cutters

4. For the overall hardened plastic mold

5. For thermosetting plastic forming, it requires high wear resistance and high strength mold


COMPOSIÇÃO

CMnSiCrW
0.94
1.200.30
0.500.50


Especificações:

Coeficiente de expansão térmica (63-64 HRC)
Temperatura︒Fin / in︒F × 10-6Temperatura︒Cmm / mm︒C × 10-6
100-5005.9638-26010.73
100-8007.1438-42712.85
100-10007.8438-53814.11
100-12008.0238-64914.44


PROPRIEDADES FÍSICAS

· Densidade: 0.283 lb / in3 (7833 kg / m3)

· Gravidade Específica: 7.83

· Módulo de elasticidade: 31 x 106 psi (214GPa)

· Usinabilidade: 85-90% de um aço carbono a 1%

Surface Finish: Black, Rough Machined,Turned or as per given requirements.

INSTRUÇÕES DE TRATAMENTO DE CALOR

ENDURECIMENTO

TEMPERATURA CRITICA:
Ac1: 1350 ° F (732 ℃)Ac3: 1440 ° F (760 ℃)
AR1: 1295 ° F (703 ℃)AR3: 1240 ° F (671 ℃)


Vantagem:

1. Little distortion after heat treatment

2. Hardness up to HRC63  

3. Good toughness, good crack-resistance


itemDimensão (mm)ExtraçãoCondição de entrega
BloquearT 20-200 X 300-800        Laminados a quente e forjados a quenteSuperfície preta / Máquina e recozimento