Dane Techniczne
Stal T1 to stal narzędziowa typu wolframu. Bardzo wysoka odporność na ścieranie i zmiękczanie. Dobra wytrzymałość i zdolność cięcia. Reakcja głębokiego utwardzania.
Szybkie Szczegóły:
T1 1.3355 ROUND BAR
SKŁAD
| C | Si | Mn | P&S | Cr | V | W |
| 0.65-0.80 | 0.20-0.40 | 0.10-0.40 | 0.03max | 3.75-4.5 | 0.90-1.30 | 17.25-18.75 |
Aplikacje:
The application is decided by T1 steel chemical composition and properties.
It is mainly used to make complex blades and impact-resistant metal cutting tools.
It can also manufacture high-temperature bearings and cold extrusion dies.
It also is used to make gear tools, milling tools, and tools such as punches, cutters and etc.
Dane techniczne:Okrągły pasek
Specification: diameter: 12mm – 220mm; length: can be customized
Surface: Black Surface/Bright Surface/ Grinded/Peeled/Turned
WŁAŚCIWOŚCI WZGLĘDNE
| Leczenie | Zakres temperatury pracy | Cooling/Quenching | Uwagi |
| Kucie | 1700-2100°F | Zwolnij | Cool slowly in dry sand or in other insulating media |
| wyżarzanie | 1600-1650°F | Cool slowly at a rate of 35° F per hour to 1000° F | For best results, insulating media is desirable. Hold at temperature for 2 hours |
| Zwalczanie stresu | 1100-1300°F | Cool slowly | Stress relieve after rough machining |
| Podgrzewanie | 1500-1550°F | Preheat time in furnace is Hr. per inch of thickness. Heating up to temperature as slow as possible | |
| hartowanie | 2325-2375° F(furnace) 2275-2350°F(salt bath) | Quench in air or warm oil. To minimize quenching strains, quench in salt at 1000° F | For maximum wear resistance, harden at 2375° F. For maximum toughness and high hardness, harden at 2275° F |
| Ruszenie | 1022° F-1058°F | Temper T1 tool steel immediately after quenching. Hold for at least 2 hours | Double tempering is recommended. The usual tempering time is 2+2 hours.Recommended temperature is 1000-1075° F for cutting tools. 1100-1200° F for shock tools |
| Pozycja | Wymiary (mm) | Przetwarzanie | Warunki dostawy |
Okrągły pasek | DIA1.0 - 30 | Ciągnienie na zimno / Szlifowanie bezkłowe | Jasne i wyżarzone |
| DIA20 - 80 | Peeling | Jasne i wyżarzone | |
| ŚREDNICA 13-180 | Walcowane na gorąco | Czarna powierzchnia i wyżarzanie | |
| ŚREDNICA 70 - 400 | Walcowane na gorąco | Czarna powierzchnia i wyżarzanie |