HSS M42 block

Molybdenum high-speed steels and tungsten high-speed steels are two types of high-speed tool steels. Molybdenum high-speed steels, also known as group M steels, comprise less initial cost. Molybdenum steel types M1 to M10 have tungsten whereas cobalt is not found in type M6. Cobalt is totally absent in these types of molybdenum high-speed steels.

M42 tool steel, a type of molybdenum high speed tool steel, has good wear resistance and hot hardness along with high hardness values.

Aplikacje:

M42 tool steel is mostly used for machine materials and super alloys that are difficult to machine. The machine materials include chasers, broaches, form and gear cutters, hobs, drills, milling cutters, end mills and taps.

Szybkie Szczegóły: M42 BLOCK， BLOCK

SKŁAD

WŁAŚCIWOŚCI WZGLĘDNE

HEAT TREATING INSTRUCTIONS： HARDENING

Podgrzewanie: Ogrzewać z szybkością nieprzekraczającą 400°F na godzinę (222°C na godzinę) do 1500-1600°F (816-871°C) i wyrównać.

Austenityzacja (wysoka temperatura): Szybko podgrzać z podgrzania.

Piec: 2150-2175°F (1177-1191°C)

Sól: 2125-2150°F (1163-1177°C)

Aby zmaksymalizować wytrzymałość, użyj najniższej temperatury.

Aby zmaksymalizować twardość na gorąco, użyj najwyższej temperatury.

Hartowanie: Gaz pod ciśnieniem, ciepły olej lub sól. W przypadku gazu pod ciśnieniem szybkie schładzanie do temperatury poniżej 1000°F

(538°C) ma kluczowe znaczenie dla uzyskania pożądanych właściwości. 

W przypadku oleju hartuj do uzyskania czerni, około 900 ° F (482 ° C), a następnie schłodź w nieruchomym powietrzu do 150 -125 ° F (66-51 ° C).

W przypadku soli utrzymywanej w temperaturze 1000-1100°F (538-593°C), wyrównać, a następnie schłodzić w nieruchomym powietrzu do 150-125°F (66-51°C).

Ruszenie: Odpuszczać natychmiast po hartowaniu. Typowy zakres odpuszczania to 950-1050°F (510-566°C). Trzymaj w temperaturze przez 2 godziny, następnie ochłodź powietrzem do temperatury otoczenia. Wymagane jest potrójne odpuszczanie.