HSS M2 1.3343 SK H9 --- Arkusze

1.3343/M2 steel is a higher carbon version of the M1 tool (molybdenum high speed steel). 1.3343 alloy has somewhat better wear resistance than M1. Very high resistance to softening at elevated temperatures. Very high resistance to wear. Good toughness and cutting capability.

Deep hardening response.

Aplikacje:

Twist drills, taps, milling cutters, reamers, broaches, saws, and different kinds of knives.

Szybkie Szczegóły:

M2/1.3343  sheets

SKŁAD

WŁAŚCIWOŚCI WZGLĘDNE

WŁAŚCIWOŚCI FIZYCZNE

· Gęstość: 0.294 funta/cal3 (8138 kg/m3)

· Ciężar właściwy: 8.14

· Moduł sprężystości: 30 x 106 psi (207GPa)

· Skrawalność: 50-60% 1% stali węglowej

INSTRUKCJE DOTYCZĄCE OBRÓBKI CIEPLNEJ

UTWARDZANIE

Podgrzewanie:To minimize distortion and stresses in large or complex tools use a double preheat.

Heat at a rate not exceeding 400°F per hour (222°C per hour) to 1100°F (593°C) equalize, then heat to 1450-1550°F (788-843°C). 

For normal tools, use only the second temperature range as a single preheating treatment.       

Ruszenie:Temperuj natychmiast po hartowaniu. Typowy zakres temperowania to 1025-1050°F (552-566°C). Utrzymać w temperaturze przez 2 godziny, a następnie schłodzić powietrzem do temperatury otoczenia. Wymagane jest podwójne hartowanie. W przypadku dużych przekrojów, a zwłaszcza półfabrykatów, z których narzędzia będą wycinane drutem EDM, zdecydowanie zaleca się potrójne odpuszczanie.

KORZYŚĆ:

1. Szybkotnąca stal narzędziowa wolframowo-molibdenowa;

2. Wysoka odporność na zużycie;

3.Wysoka dekarbonizacja.