H13 1.2344 SKD61

Id-dar>prodotti>Azzar tal-Għodda tax-Xogħol Jaħraq>H13 1.2344 SKD61

H13 1.2344 SKD61 bar ċatt

Ikkuntatjana

speċifikazzjonijiet

H13 Tool Steel is a versatile chromium-molybdenum hot work steel that is widely used in hot work and cold work tooling applications. The hot hardness (hot strength) of H13 resists thermal fatigue cracking which occurs as a result of cyclic heating and cooling cycles in hot work tooling applications. Because of its excellent combination of high toughness and resistance to thermal fatigue cracking (also known as heat checking) H13 is used for more hot work tooling applications than any other tool steel.

Because of its high toughness and very good stability in heat treatment, H13 is also used in a variety of cold work tooling applications. In these applications, H13 provides better hardenability (through hardening in large section thicknesses) and better wear resistance than common alloy steels such as 4140.

Also available as Electro-Slag-Remelted (ESR) and Vacuum-Arc-Remelted (VAR) products as well. The remelting processes provide improved chemical homogeneity, refinement of carbide size, and the associated improvements in mechanical properties and fatigue properties.

APPLIKAZZJONIJIET:Inserts, qlub, u kavitajiet għal die casting die, kmiem ta 'sparatura die casting, forging sħun imut, dies ta' estrużjoni, u kavitajiet ta 'moffa tal-plastik u komponenti li jeħtieġu ebusija għolja u polishability eċċellenti.

KOMPOŻIZZJONI

C

Mn

Si

Cr

Mo

V

0.40

0.40

1.00

5.25

1.35

1.00


Konduttività Termali

Temperatura︒F

Btu / hr-ft︒F

Temperatura︒C

W / m︒C

80

10.17

27

17.6

400

13.52

204

23.4

800

14.5

427

25.1

1200

15.49

649

26.8

PROPRJETAJIET FIŻIĊI

· Densità: 0.280 lb/in3 (7750 kg/m3)

· Gravità Speċifika: 7.75

· Makkinabilità: 65-70% ta 'azzar tal-karbonju ta' 1%.

Modulu ta 'Elastiċità

Temp︒F

Modulus psi×10-6

Temp︒C

Modulus Gpa

70

30.0

21

206.8

200

29.0

93

199.9

400

27.0

204

186.2

600

28.5

316

196.5

800

27.5

427

189.6

1000

23.0

538

158.6

 

Koeffiċjent ta 'Espansjoni Termali (47-48 HRC)

Temperatura︒F

fi/in︒F×10-6

Temperatura︒C

mm/mm︒C×10-6

80-200

5.8

21-93

10.4

80-400

6.3

21-204

11.3

80-800

6.9

21-316

12.4

80-1200

7.3

21-427

13.1

80-1500

7.5

21-538

13.


1492431268787984


STRUZZJONIJIET GĦAT - TRATTAMENT TAS - SĦANA

TISĦIĦ

TEMPERATURA KRITIKA :

Ac1: 1544 ° F (840 ℃)

Ac3: 1634 ° F (890 ℃)

AR1: 1475 ° F (802 ℃)

AR3: 1418 ° F (826 ℃)

Sħana minn qabel: Biex timminimizza d-distorsjoni f'għodod kumplessi uża preheat doppju. Saħħan b'rata li ma taqbiżx 400°F fis-siegħa (222°C fis-siegħa) għal 1150-1250°F (621-677°C), ekwivalja, imbagħad żid għal 1500-1600°F (816-871°C) u indaqs. Għal għodod normali, uża biss it-tieni medda ta 'temperatura bħala trattament wieħed ta' tisħin minn qabel.

Austenitizing (High Heat): Heat rapidly from the preheat. Furnace or Salt: 1800-1890°F (982-1032°C) For maximum toughness, use 1800°F (982°C) For maximum hardness and resistance to thermal fatigue cracking and wear use 1890 (1032°C). Soak at temperature for 30 to 90 minutes.

Tifi: Arja, gass taħt pressjoni, jew żejt sħun. Ħxuna tas-sezzjonijiet sa u inklużi 5 pulzieri (127 mm) tipikament jibbies kompletament meta jitkessaħ f'arja kwieta mit-trattament ta' awstenitizzazzjoni. Sezzjonijiet ta 'ħxuna akbar minn 5 pulzieri (127 mm) se jeħtieġu tkessiħ aċċellerat billi tuża arja sfurzata, gass taħt pressjoni, jew quench taż-żejt interrott biex tinkiseb ebusija, toughness u reżistenza massima għall-qsim tal-għeja termali.

Għat-tifi tal-gass taħt pressjoni, rata minima ta 'quench ta' madwar 50 ° F kull minuta (28 ° C kull minuta) sa taħt 1000 ° F (538 ° C) hija meħtieġa biex jinkisbu l-aħjar proprjetajiet fl-azzar.

Għaż-żejt, quench sakemm iswed, madwar 900 ° F (482 ° C), imbagħad kessaħ f'arja kwieta għal 150-125 ° F (66-51 ° C).

Ittemprar: Ittempru immedjatament wara t-tifi. Il-firxa tipika tat-tempra hija ta '1000-1150 ° F (538-621 ° C). Żomm fit-temperatura tat-tempering għal siegħa kull pulzier (1mm) ta 'ħxuna, iżda għal sagħtejn minimi, imbagħad kessaħ bl-arja sat-temperatura ambjentali. Huwa meħtieġ ittemprar doppju. Biex timmassimizza l-ebusija u l-prestazzjoni tal-għodda, it-tielet temper huwa spiss użat bħala serħan mill-istress wara li l-makkinar kollu tat-tlestija, it-tħin u x-xogħol EDM jitlestew fuq l-għodda.

ANNESS

L-ittemprar għandu jsir wara xogħol sħun u qabel it-twebbis mill-ġdid.

Saħħan b'rata li ma taqbiżx 400 ° F fis-siegħa (222 ° C fis-siegħa) sa 1575-1625 ° F (857-885 ° C), u żomm f'temperatura għal siegħa kull pulzier ta 'ħxuna massima; Sagħtejn minimu. Imbagħad kessaħ bil-mod bil-forn b'rata li ma taqbiżx il-1 ° F fis-siegħa (2 ° C fis-siegħa) sa 50 ° F (28 ° C). Kompli kessaħ għal temperatura ambjentali fil-forn jew fl-arja. L-ebusija li tirriżulta għandha tkun massimu ta '1000 HBS.


PuntDimensjoni (mm)ProċessKondizzjoni tal-kunsinna
Bar tondDIA1.0 - 30Tpinġija kiesħa / tħin bla ċentruBright & Anneal
DIA20 - 80TqaxxirBright & Anneal
DIA 13-180Irrumblat bis-sħanaWiċċ iswed u Anneal
DIA 70 - 400Irrumblat bis-sħanaWiċċ iswed u Anneal
Bar ĊattT 3.0-20 XW 20-100Irrumblat bis-sħanaWiċċ iswed u Anneal
BlokkT 20-200 X 300-800Hot Rolled & Hot FalsifikatiWiċċ iswed / Magna & Anneal
Virga tal-wajerDIA 5.5 - 13Irrumblat bis-sħanaWiċċ iswed u Anneal
FoljiT1.0 - 2.5Irromblati kesħinWiċċ iswed u Anneal
T 2.5 - 8.0Irrumblat bis-sħanaWiċċ iswed u Anneal