O1 1.2510 SKS3

Нүүр хуудас>Бүтээгдэхүүн>Хүйтэн ажлын багаж>O1 1.2510 SKS3

O1 1.2510 SKS3 блок

Холбоо барих

үзүүлэлт нь
O1 Tool Steel is the original oil-hardening, “non-shrinking” tool steel that can be hardened to the Rockwell C 65 range from a low austenitizing temperature. O1 is a general-purpose tool steel that is typically used in applications where alloy steels cannot provide sufficient hardness, strength, and wear resistance.

Програм: Where greater dimensional stability in heat treatment or improved wear resistance is required, tool steels with higher alloy contents, such as A2 or D2 should be considered.

Бүрэлдэхүүн хэсэг

C

Mn

Si

Cr

W

0.94

1.20

0.30

0.50

0.50

ХОЛБООТОЙ ХӨРӨНГӨ

1492433770224674

Дулааны өргөтгөлийн коэффициент (63-64 HRC)

Температур: F

in × in × 10-6

Температур︒C

мм / мм︒C × 10-6

100-500

5.96

38-260

10.73

100-800

7.14

38-427

12.85

100-1000

7.84

38-538

14.11

100-1200

8.02

38-649

14.44

Физикийн өмч

· Нягт: 0.283 фунт / ин3 (7833 кг / м3)

· Тодорхой таталцал: 7.83

· Мэдрэмжийн модуль: 31 x 106 psi (214GPa)

· Машинаар боловсруулах чадвар: 85% нүүрстөрөгчийн гангийн 90-1%

1492433836447736

Дулааны эмчилгээний хариу арга хэмжээ

Агаарын хөргөлт

HRC

1425F (774︒C), 30 минут

62

1450F (788︒C), 30 минут

64

1475F (802︒C), 30 минут

65

1500F (816︒C), 30 минут

65

1600F (871︒C), 30 минут

64

ДУЛААНЫГ ЭРЧИЛГЭХ ЗААВАР

ХАТУУЛАХ

ШУУРХАЙ ТЕМПЕРАТУР:

Ac1: 1350 ° F (732 ℃))

Ac3: 1440 ° F (760 ℃))

AR1: 1295 ° F (703 ℃))

AR3: 1240 ° F (671 ℃))

Урьдчилан халаах: Нэг цагт 400 ° F (цагт 222 ° C) -аас хэтрэхгүй хэмжээгээр 1200-1300 ° F (649-704 ° C) хүртэл халааж, тэнцүү болгоно.

Austenitizing (High Heat): Heat slowly from the preheat to 1475-1500°F (802-816C)

Эхний инч (30 мм) зузаантай бол 25.4 минут, нэмэлт инч (15 мм) тус бүрт 25.4 минут байлгана.

Бөхөөх: Тосыг 150-125 ° F (66-51 ° C) -аас багагүй температурт унтраана.

Note: O1 is somewhat prone to quench cracking, especially if there are significant changes in section thickness and sharp internal corners. The oil quenching should be performed so that the heat removal is as uniform as possible in all areas of the part being quenched. Be sure to remove the part from the oil before the temperature drops to ambient temperature. Hot oil at a temperature of 300 to 400°F (149-204°C) is recommended.

Уурлах: Temper immediately after quenching. Do not allow the part to cool below 125°F (51°C). The typical tempering range is 350 - 400°F (177 -204°C). Hold at temperature for 1 hour per inch (25.4 mm) of thickness, 2 hours minimum, then air cool to ambient temperature. To minimize internal stresses in cross sections greater than 3 inches (76.2 mm) and to improve stability in parts that will be EDM’d after heat treatment, a soaking time of 4 to 6 hours at the tempering temperature is strongly recommended.

Cryogenic Treatment: Refrigeration treatments should typically be performed after the temper, and must be followed by a second temper.

ХӨЛБӨР

Шатаах ажлыг халуун ажлын дараа дахин хатууруулахаас өмнө хийх шаардлагатай.

Heat at a rate not exceeding 400°F per hour (222°C per hour) to 1425 -1450°F (802-816°C), and hold at temperature for 1 hour per inch (25.4mm) of maximum thickness; 2 hours minimum. Then cool slowly with the furnace at a rate not exceeding 50°F per hour (28°C per hour) to 1000°F (538°C). Continue cooling to ambient temperature in the furnace or in air. The resultant hardness should be a maximum of 212 HBW.

БарааныХэмжээ (мм)үйл явцХүргэлтийн нөхцөл
Round BarDIA 1.0 - 30Хүйтэн зураг / Төвгүй нунтаглахBright & Anneal
DIA 20 - 80хоёр талд нь хэвлэхBright & Anneal
DIA 13-180Халуун цувисанХар гадаргуу ба Anneal
DIA 70-400Халуун цувисанХар гадаргуу ба Anneal
Хавтгай барT 3.0-20 XW 20-100Халуун цувисанХар гадаргуу ба Anneal
БлокT 20-200 X 300-800Халуун цувисан ба халуун хуурамчХар гадаргуу / Machine & Anneal
Утсан савааDIA 5.5-13Халуун цувисанХар гадаргуу ба Anneal
хуудасT1.0 - 2.5Хүйтэн цувисанХар гадаргуу ба Anneal
T 2.5 - 8.0Халуун цувисанХар гадаргуу ба Anneal