D2 1.2379 SKD11

Нүүр хуудас>Бүтээгдэхүүн>Хүйтэн ажлын багаж>D2 1.2379 SKD11

D2 1.2379 SKD11 хавтгай баар

Холбоо барих

үзүүлэлт нь
D2 Tool Steel is a versatile high-carbon, high-chromium, air-hardening tool steel that is characterized by a relatively high attainable hardness and numerous, large, chromium-rich alloy carbides in the microstructure. These carbides provide good resistance to wear from sliding contact with other metals and abrasive materials. Although other steels with improved toughness or improved wear resistance are available, D2 provides an effective combination of wear resistance and toughness, tool performance, price, and a wide variety of product forms. Also available as an Electro-Slag-Remelted (ESR) product. The remelting process provides improved chemical homogeneity, refinement of carbide size, and the associated improvements in mechanical and fatigue properties.

Програм: Өнхрөх, цоолох, хоосон болгох, хэлбэржүүлэх, шүргэх, утас өнхрүүлэх, хайч хутга, хоол боловсруулах хутга, хэмжигч зэрэгт үхдэг.

Бүрэлдэхүүн хэсэг

C

Mn

Si

Cr

Mo

V

1.50

0.30

0.30

12.00

0.75

0.90


ХОЛБООТОЙ ХӨРӨНГӨ

1492431879960282

Дулааны өргөтгөлийн коэффициент (58-59 HRC)

Температур: F

in × in × 10-6

Температур︒C

мм / мм︒C × 10-6

100-500

5.71

38-260

10.3

100-800

6.63

38-427

11.9

100-1000

6.82

38-538

12.3

100-1200

6.83

38-649

12.3

100-1500

6.9

38-816

12.4

Физикийн өмч

· Нягт: 0.278 фунт / ин3 (7695 кг / м3)

· Тодорхой таталцал: 7.70

· Мэдрэмжийн модуль: 30 x 106 psi (207GPa)

· Машинаар боловсруулах чадвар: 50% нүүрстөрөгчийн гангийн 60-1%

1492431918971275

ДУЛААНЫГ ЭРЧИЛГЭХ ЗААВАР

ХАТУУЛАХ

ШУУРХАЙ ТЕМПЕРАТУР:

Ac1: 1449 ° F (788 ℃))

Ac3: 1553 ° F (845 ℃))

AR1: 1418 ° F (769 ℃))

AR3: 1373 ° F (744 ℃))

Урьдчилан халаах: To minimize distortion and stresses in large or complex tools use a double preheat. Heat at a rate not exceeding 400°F per hour (222°C per hour) to 1150-1250°F (621-677°C) equalize, then heat to 1400-1450°F (760-788°C). For normal tools, use only the second temperature range as a single preheating treatment.

Агааржуулагч (Өндөр дулаан): Heat slowly from the preheat. Furnace or Salt: 1850-1875°F (1010-1024°C).

Quenching: Air or pressurized gas to 150-125ºF (66-51ºC). Sizes up to 4 inches (101.6 mm) in thickness will through harden when air cooled from 1575ºF (857ºC). Sizes up to 6 inches (152.4 mm) in thickness will through harden when air cooled from 1625ºF (885ºC).

Уурлах: Temper immediately after quenching. Hold at temperature for 1 hour per inch (25.4 mm) of thickness, 2 hours minimum, then air cool to ambient temperature. The typical tempering range is 350 to 400ºF (177 to 204ºC).

Хамгийн их элэгдэлд тэсвэртэй байхын тулд 300-350 HRC-ийн хатуулагтай үед 149-177 ° F (62-64 ° C) температурт халаана. Элэгдэлд тэсвэртэй ба хатуулаг хоорондын оновчтой тэнцвэрийг хадгалахын тулд 500-550 ° F (260-288 ° C) температурыг хадгална. Энэ нь 58-60 HRC үйлдвэрлэх болно.

For maximum toughness, double temper, 2 hours plus 2 hours, at temperatures above 950°F (510°C). This will produce hardness of less than 58 HRC.

To minimize internal stresses in cross sections greater than 6 inches (152.4 mm) and to improve stability in tools that will be EDM'd after heat treatment, soaking times of 4 to 6 hours at the tempering temperature below 950°F (510°C) are strongly recommended.

Анхан шатны тусламж үйлчилгээ: Annealing must be performed after hot working and before re-hardening. Heat at a rate not exceeding 400°F per hour (222°C per hour) to 1600-1650°F (871-899°C), and hold at temperature for 1 hour per inch (25.4mm) of maximum thickness; 2 hours minimum. Then cool slowly with the furnace at a rate not exceeding 50°F per hour (28°C per hour) to 1000°F (538°C). Continue cooling to ambient temperature in the furnace or in air. The resultant hardness should be a maximum of 255 HBW.

БарааныХэмжээ (мм)үйл явцХүргэлтийн нөхцөл
Round BarDIA 1.0 - 30Хүйтэн зураг / Төвгүй нунтаглахBright & Anneal
DIA 20 - 80хоёр талд нь хэвлэхBright & Anneal
DIA 13-180Халуун цувисанХар гадаргуу ба Anneal
DIA 70-400Халуун цувисанХар гадаргуу ба Anneal
Хавтгай барT 3.0-20 XW 20-100Халуун цувисанХар гадаргуу ба Anneal
БлокT 20-200 X 300-800Халуун цувисан ба халуун хуурамчХар гадаргуу / Machine & Anneal
Утсан савааDIA 5.5-13Халуун цувисанХар гадаргуу ба Anneal
хуудасT1.0 - 2.5Хүйтэн цувисанХар гадаргуу ба Anneal
T 2.5 - 8.0Халуун цувисанХар гадаргуу ба Anneal