T1 болоту вольфрам тибиндеги шайман болот. Тактоого жана жумшартууга өтө жогорку туруктуулук. Жакшы бышыктык жана кесүү мүмкүнчүлүгү. Deep hardening response.


Quick Толугураак:

T1 1.3355 ROUND BAR 

Курамы

CSiMn
P&S
Cr
V
W
0.65-0.80
0.20-0.40
0.10-0.40
0.03max
3.75-4.50.90-1.30
17.25-18.75


Тиркемелер:

The application is decided by T1 steel chemical composition and properties. 

It is mainly used to make complex blades and impact-resistant metal cutting tools. 

It can also manufacture high-temperature bearings and cold extrusion dies. 

It also is used to make gear tools, milling tools, and tools such as punches, cutters and etc.


өзгөчөлүктөрү:тегерек Bar

Specification: diameter: 12mm – 220mm; length: can be customized

Surface: Black Surface/Bright Surface/ Grinded/Peeled/Turned

       

САЛЫШТЫК КАСИЕТТЕР

иштетүү       Temperature RangeCooling/Quenchingжазуулар
жасалмалоо1700-2100 ° FжайCool slowly in dry sand or in other insulating media
Annealing1600-1650 ° FCool slowly at a rate of 35° F per hour to 1000° FFor best results, insulating media is desirable. Hold at temperature for 2 hours
стресс бошотуу1100-1300 ° FCool slowlyStress relieve after rough machining
Алдын ала ысытуу1500-1550 ° F
Preheat time in furnace is Hr. per inch of thickness. Heating up to temperature as slow as possible
катуу2325-2375° F(furnace) 2275-2350°F(salt bath)Quench in air or warm oil. To minimize quenching strains, quench in salt at 1000° FFor maximum wear resistance, harden at 2375° F. For maximum toughness and high hardness, harden at 2275° F
жумшартуу1022° F-1058°FTemper T1 tool steel immediately after quenching. Hold for at least 2 hoursDouble tempering is recommended. The usual tempering time is 2+2 hours.Recommended temperature is 1000-1075° F for cutting tools. 1100-1200° F for shock tools


нерсеDimension (мм)ProcessЖеткирүү шарты

тегерек Bar

DIA1.0 - 30Муздак тартуу / Борборсуз майдалооBright & Anneal
DIA20 - 80пилингBright & Anneal
DIA 13-180Hot RolledКара бет жана Anneal
DIA 70 - 400Hot RolledКара бет жана Anneal