D2 1.2379 SKD11 flatstöng

Hafðu samband

upplýsingar
D2 Tool Steel is a versatile high-carbon, high-chromium, air-hardening tool steel that is characterized by a relatively high attainable hardness and numerous, large, chromium-rich alloy carbides in the microstructure. These carbides provide good resistance to wear from sliding contact with other metals and abrasive materials. Although other steels with improved toughness or improved wear resistance are available, D2 provides an effective combination of wear resistance and toughness, tool performance, price, and a wide variety of product forms. Also available as an Electro-Slag-Remelted (ESR) product. The remelting process provides improved chemical homogeneity, refinement of carbide size, and the associated improvements in mechanical and fatigue properties.

UMSÓKNIR: Rúllur, kýlingar, stansar til að teygja, móta, klippa og tvinna þráð, klippa hnífa, matvælavinnsluhnífa og mæla.

Samsetning

C

Mn

Si

Cr

Mo

V

1.50

0.30

0.30

12.00

0.75

0.90


TENGDIR EIGINLEIKAR

1492431879960282

Stuðull hitaþenslu (58-59 HRC)

Hitastig︒F

í / in︒F × 10-6

Hitastig︒C

mm / mm︒C × 10-6

100-500

5.71

38-260

10.3

100-800

6.63

38-427

11.9

100-1000

6.82

38-538

12.3

100-1200

6.83

38-649

12.3

100-1500

6.9

38-816

12.4

LÍKAMLEGIR EIGINLEIKAR

· Þéttleiki: 0.278 lb / in3 (7695 kg / m3)

· Sérstakur þyngdarafl: 7.70

· Mýktarstuðull: 30 x 106 psi (207GPa)

· Vélarhæfileiki: 50-60% af 1% kolefni stáli

1492431918971275

LEIÐBEININGAR um hitun

HERÐUN

GAGNRÆN HITA :

Ac1: 1449 ° F (788 ℃)

Ac3: 1553 ° F (845 ℃)

AR1: 1418 ° F (769 ℃)

AR3: 1373 ° F (744 ℃)

Forhitun: To minimize distortion and stresses in large or complex tools use a double preheat. Heat at a rate not exceeding 400°F per hour (222°C per hour) to 1150-1250°F (621-677°C) equalize, then heat to 1400-1450°F (760-788°C). For normal tools, use only the second temperature range as a single preheating treatment.

Austenitizing (hár hiti): Hitið hægt af forhituninni. Ofn eða salt: 1850-1875°F (1010-1024°C).

Quenching: Air or pressurized gas to 150-125ºF (66-51ºC). Sizes up to 4 inches (101.6 mm) in thickness will through harden when air cooled from 1575ºF (857ºC). Sizes up to 6 inches (152.4 mm) in thickness will through harden when air cooled from 1625ºF (885ºC).

Hitun: Hitaðu strax eftir slökkvun. Haltu við hitastig í 1 klukkustund á hverja tommu (25.4 mm) af þykkt, 2 klukkustundir að lágmarki, síðan loftkælt niður í umhverfishita. Dæmigerð hitastigssvið er 350 til 400ºF (177 til 204ºC).

Til að fá hámarks slitþol, tempraðu á bilinu 300-350°F (149-177°C) fyrir hörku 62-64 HRC. Til að ná sem bestum jafnvægi milli slitþols og seigleika, tempraðu á milli 500-550°F (260-288°C). Þetta mun framleiða 58-60 HRC.

Fyrir hámarks hörku, tvöfaldur skapur, 2 klst plús 2 klst, við hitastig yfir 950°F (510°C). Þetta mun framleiða hörku undir 58 HRC.

To minimize internal stresses in cross sections greater than 6 inches (152.4 mm) and to improve stability in tools that will be EDM'd after heat treatment, soaking times of 4 to 6 hours at the tempering temperature below 950°F (510°C) are strongly recommended.

Glæðing: Hreinsun verður að fara fram eftir heita vinnslu og áður en endurherð er. Hitið á hraða sem fer ekki yfir 400°F á klukkustund (222°C á klukkustund) í 1600-1650°F (871-899°C), og haldið við hitastig í 1 klukkustund á tommu (25.4 mm) af hámarksþykkt; 2 klst lágmark. Kældu síðan hægt með ofninum á hraða sem fer ekki yfir 50°F á klukkustund (28°C á klukkustund) til 1000°F (538°C). Haltu áfram að kæla niður í umhverfishita í ofninum eða í lofti. Hörku sem myndast ætti að vera að hámarki 255 HBW.

LiðurMál (mm)aðferðAfhendingarskilyrði
Round BarDIA1.0 - 30Kaldteikning / miðlaus malaBright & Anneal
DIA20 - 80FlagnaBright & Anneal
DIA 13-180Heitt valsaðSvart yfirborð & Anneal
DIA 70 - 400Heitt valsaðSvart yfirborð & Anneal
Flat barT 3.0-20 XW 20-100Heitt valsaðSvart yfirborð & Anneal
LokaðT 20-200 X 300-800Hot Rolled & Hot ForgedSvart yfirborð / Machine & Anneal
VírstöngullDIA 5.5 - 13Heitt valsaðSvart yfirborð & Anneal
SheetsT1.0 - 2.5KaldvalsaðSvart yfirborð & Anneal
T 2.5 - 8.0Heitt valsaðSvart yfirborð & Anneal
Hafðu samband við okkur