O1 1.2510 SKS3 lohko

O1 Tool Steel is the original oil-hardening, “non-shrinking” tool steel that can be hardened to the Rockwell C 65 range from a low austenitizing temperature. O1 is a general-purpose tool steel that is typically used in applications where alloy steels cannot provide sufficient hardness, strength, and wear resistance.

KÄYTTÖKOHTEET: Jos lämpökäsittelyssä vaaditaan suurempaa mittastabiilisuutta tai parempaa kulutuskestävyyttä, tulee harkita työkaluteräksiä, joissa on korkeampi seosainepitoisuus, kuten A2 tai D2.

KOKOONPANO

C	Mn	Si	Cr	W
0.94	1.20	0.30	0.50	0.50

SUHTEELLISET OMINAISUUDET

Lämpölaajenemiskerroin (63-64 HRC)
Lämpötila︒F	in / in︒F × 10-6	Lämpötila ︒C	mm / mm︒C × 10-6
100-500	5.96	38-260	10.73
100-800	7.14	38-427	12.85
100-1000	7.84	38-538	14.11
100-1200	8.02	38-649	14.44

FYSIKAALISET OMINAISUUDET

· Tiheys: 0.283 kg / m3 (7833 lb / in3)

· Ominaispaino: 7.83

· Elastisuusmoduuli: 31 x 106 psi (214GPa)

· Koneistettavuus: 85-90% 1% hiiliterästä

Lämpökäsittelyvaste
Ilmajäähdytetty	HRC
1425F (774 ° C), 30 minuuttia	62
1450F (788 ° C), 30 minuuttia	64
1475F (802 ° C), 30 minuuttia	65
1500F (816 ° C), 30 minuuttia	65
1600F (871 ° C), 30 minuuttia	64

LÄMPÖKÄSITTELYOHJEET

Kovettuminen

KRIITTINEN LÄMPÖTILA ：
Ac1: 1350 ° F (732 ℃)	Ac3: 1440 ° F (760 ℃)
AR1: 1295 ° F (703 ℃)	AR3: 1240 ° F (671 ℃)

Esilämmitys: Lämmitä nopeudella, joka ei ylitä 400 ° F tunnissa (222 ° C tunnissa) 1200-1300 ° F: seen (649-704 ° C) ja tasaantuu.

Austenitizing (High Heat): Heat slowly from the preheat to 1475-1500°F (802-816C)

Liota 30 minuuttia ensimmäisen tuuman (25.4 mm) paksuudeksi ja 15 minuuttia jokaista seuraavaa tuumaa (25.4 mm) kohti.

Sammutus: Öljy sammutetaan vähintään lämpötilaan 150 - 125 ° F (66 - 51 ° C).

Note: O1 is somewhat prone to quench cracking, especially if there are significant changes in section thickness and sharp internal corners. The oil quenching should be performed so that the heat removal is as uniform as possible in all areas of the part being quenched. Be sure to remove the part from the oil before the temperature drops to ambient temperature. Hot oil at a temperature of 300 to 400°F (149-204°C) is recommended.

Karkaisu: Temper immediately after quenching. Do not allow the part to cool below 125°F (51°C). The typical tempering range is 350 - 400°F (177 -204°C). Hold at temperature for 1 hour per inch (25.4 mm) of thickness, 2 hours minimum, then air cool to ambient temperature. To minimize internal stresses in cross sections greater than 3 inches (76.2 mm) and to improve stability in parts that will be EDM’d after heat treatment, a soaking time of 4 to 6 hours at the tempering temperature is strongly recommended.

Cryogenic Treatment: Refrigeration treatments should typically be performed after the temper, and must be followed by a second temper.

hehkutus

Hehkutus on suoritettava kuuman työn jälkeen ja ennen kovettamista.

Heat at a rate not exceeding 400°F per hour (222°C per hour) to 1425 -1450°F (802-816°C), and hold at temperature for 1 hour per inch (25.4mm) of maximum thickness; 2 hours minimum. Then cool slowly with the furnace at a rate not exceeding 50°F per hour (28°C per hour) to 1000°F (538°C). Continue cooling to ambient temperature in the furnace or in air. The resultant hardness should be a maximum of 212 HBW.

erä	Mitat (mm)	Käsitellä asiaa	Toimitusehto
Pyöreä palkki	DIA1.0-30	Kylmäveto / keskittämätön hionta	Kirkas & hehkuttaa
	DIA20-80	Kuorinta	Kirkas & hehkuttaa
	DIA 13-180	Kuumavalssattu	Musta pinta ja hehkutus
	DIA 70-400	Kuumavalssattu	Musta pinta ja hehkutus
Litteä baari	T 3.0-20 XW 20-100	Kuumavalssattu	Musta pinta ja hehkutus
Tukkia	T 20-200 X 300-800	Kuumavalssattu ja taottu	Musta pinta / Machine & Anneal
Vaijerilanka	DIA 5.5-13	Kuumavalssattu	Musta pinta ja hehkutus
Sheets	T1.0 - 2.5	Kylmävalssattu	Musta pinta ja hehkutus
	T 2.5 - 8.0	Kuumavalssattu	Musta pinta ja hehkutus