Cold Working Tool Steel D3 1.2080 SKD1 flat bar

D3 Tool Steel is a high-carbon, high-chromium, oil-hardening tool steel that is characterized by a relatively high attainable hardness and numerous, large, chromium-rich alloy carbides in the microstructure. These carbides provide good resistance to wear from sliding contact with other metals and abrasive materials.

D3 exhibits excellent stability in heat treatment, holding size almost as well as the air-hardening, high-carbon, high-chromium die steels such as D2.

Sovellukset:

1.For the production of cold dies and punches that are subject to low impact loads, small to medium production volumes, and require high wear resistance.

2. Cold cutting blade for cutting hard and thin metal

3. For drill sleeves, gauges, wire drawing dies, embossing dies, crepe plates, drawing dies, cold extrusion dies and screw roller dies

4. Suitable for the production of large, complex and precision plastic moulds requiring high resistance

KOKOONPANO

Tekniset tiedot:

FYSIKAALISET OMINAISUUDET

· Tiheys: 0.284 kg / m3 (7870 lb / in3)

· Ominaispaino: 7.87

· Joustavuusmoduuli: 30 x 106 psi (207GPa)

· Electrical Resistivity: 54.8 uOhm-cm at 70ºF (21ºC)

· Koneistettavuus: 45-50% 1% hiiliterästä

Esilämmitys:To minimize distortion and stresses in large or complex tools use a double preheat. Heat at a rate not exceeding 400°F per hour (222°C per hour) to 1200-1250°F (649-677°C) equalize, then heat to 1400-1450°F (760-788°C). For normal tools, use only the first temperature range as a single preheating treatment.

Austenitizing (High Heat): Heat slowly from the preheat to 1700-1750°F (927-954°C)

Sammutus:Öljyn osalta sammutetaan mustaksi, noin 900 ° F (482 ° C), sitten jäähdytetään vielä ilmassa 150 - 125 ° C: seen.

For pressurized gas, the furnace should have a minimum quench pressure of 4 bars. A quench rate of approximately 400°F (222°C) per minute to below 1000°F (538°C) is critical to obtain the desired properties.

Karkaisu:Temper heti sammutuksen jälkeen. Pidä lämpötilassa 1 tunti tuumaa (25.4 mm) paksuudelta, vähintään 2 tuntia, sitten jäähdytä ilma ympäristön lämpötilaan.

Parhaan kulutuskestävyyden saavuttamiseksi lämpötila on 300-350 ° F (149-177 ° C) ja kovuus 62-63 HRC. Optimaalinen tasapaino kulutuskestävyyden ja sitkeyden välillä on lämpötilan ollessa 450-500 ° C (232-260 ° F). Tämä tuottaa 58-60 HRC.

Sisäisten jännitysten minimoimiseksi yli 6 mm: n poikkileikkauksissa ja vakauden parantamiseksi työkaluissa, jotka ovat EDM: ää lämpökäsittelyn jälkeen, 152.4 - 4 tunnin liotusajat karkaisulämpötilassa ovat erittäin suositeltavia.

Etu:

1.High abrasive resistance and small shock load

2. High wear resistance against abrasive and adhesive wear

3. Medium toughness

4.Dimensionally stable

Korkea puristuslujuus