O1 1.2510 SKS3

Home>Products>Acciaiu di Strumenti di travagliu à Fretu>O1 1.2510 SKS3

Strumentu di travagliu à fretu Steel O1 1.2510 SKS3 fogli

Cuntatta ci

quaternu di carichi

O1 tool steel is a low alloy cold work tool steel that must be oil-quenched in heat treatment. O1 tool steel contains small amounts of manganese, tungsten, and chromium, giving O1 tool steel adequate toughness for normal tool & die uses. O1 tool steel has deep hardening properties with fine grain structure with unusual toughness. O1 tool steel has good response to heat treatment with small dimensional changes. Sizes over approximately 2 inches thick or round may exhibit a lower hardness in the interior. O1 tool steel is available in standard de-carb free rounds, flats and squares, as well as the largest size selection in ground flat stock and drill rod of all the tool steel grades.


Induve una stabilità dimensionale più grande in u trattamentu termale o una resistenza à l'usura mejorata hè necessaria, deve esse cunsideratu acciai d'utensili cù un cuntenutu di lega più altu, cum'è A2 o D2.



quaternu di carichi:

ASTM O1 Tool Steel Mechanical Properties

Hardness, Brinell (soft annealed -delivery condition)190190
Hardness, Rockwell C (tempering temp 300-1200°F)34.0-64.034.0-64.0
Elastic modulus (hardened to 62 HRC)193 GPa28000 ksi
Elastic modulus (@399°C/750°F, hardened to 62 HRC )172 GPa25000 ksi
Elastic modulus (@191°C/375°F, hardened to 62 HRC)186 GPa27000 ksi
Compressive yield strength (0.2%, hardened to 50 HRC)1350 mpa196000 psi
Compressive yield strength (0.2%, hardened to 55 HRC)1800 mpa261000 psi
Compressive yield strength (0.2%, hardened to 60 HRC)2150 mpa312000 psi
Compressive yield strength (0.2%, hardened to 62 HRC)2200 mpa319000 psi

Propizziu Fisiche

Density (hardened to 62 HRC)7.81 g / cm30.282 lb / in3
Density (@399°C/ 750°F, hardened to 62 HRC)7.70 g / cm30.278 lb / in3
Density (@191°C/ 375°F, hardened to 62 HRC)7.75 g / cm30.280 lb / in3
Pianu di Melting1421 ° C2590 ° F

Pruprietà termale

T (°C)Stu travagliu
Espansione termica10.6 x 10-6/ºC20-260-

Forging of ASTM O1 Tool Steel

Heating for forging of oil tool steel O1 must be done slowly and uniformly. Forging of alloy O1 steels can be performed at 980-1000°C, and reheat as often as necessary. But not forge below 800°C. After forging AISI O1 tool steel, cool slowly in lime, mica, dry ashes or furnace. ASTM O-1 tool steels should always be annealed after forging.

AISI O1 Tool Steel Heat Treatment


L'annullamentu deve esse realizatu dopu à u travagliu caldu è prima di rinfurzà.

Heat at a rate not exceeding 222°C per hour to 802-816°C, and hold at temperature for 1 hour per inch (25.4mm) of maximum thickness; 2 hours minimum. Then cool slowly with the furnace at a rate not exceeding 28°C per hourto 538°C. Continue cooling to ambient temperature in the furnace or in air. The resultant hardness should be a maximum of 212 HBW.

Stress Relief of Unhardened Material

Heat slowly to 1250° F. Soak for two hours per inch of thickness at heat. Slow cool (furnace cool if possible) to room temperature.


1.Preheat: Warm slightly before charging into the preheat furnace, which should be operating at about 1100°-1200°F.

2.Hardening: Heat to 1475 to 1500° F. Soak at heat for 30 minutes per inch of thickness.

3.Quench: Quench O1 steel in warm oil and allow to cool in the oil until a temperature of 125°-150°F has been reached, or to where the part can be held in the bare hand, and temper immediately.

4.Temper: Normally oil hardening steels need to be single tempered only. However, double tempering may sometimes be preferred. Soak at heat for 2 hours per inch of thickness for each temper. Air cool to room temperature between tempers. The normal tempering range for this grade is 300 to 450° F.

 Stress Relief Temper

A stress relief temper for hardened material is strongly recommended after significant grinding, or welding, or EDM. Select a temperature that is 25 or 50° F lower than the last tempering temperature used.

 ItemDimensioni (mm)prucessuCundizione di consegna
FullesT1.0 - 2.5Ghjuvatu fridduSuperficie nera & Anneal
T 2.5 - 8.0Rolled HotSuperficie nera & Anneal