L2 1.2210

Home>Products>Acciaiu di Strumenti di travagliu à Fretu>L2 1.2210

Strumentu di travagliu à fretu in acciaio Mat.No. 1.2210, DIN 115CrV3, barra tonda AISI L2

Cuntatta ci

quaternu di carichi

Designazione per Standards

Mat. Innò.DINENAISI
1.2210115CrV3-L2

Composizione chimica (in %)

CSiMnCrMoNiVWOtros
1.170.230.300.65--0.10--

Description:

Low alloyed cold working tool steel.

Appricazzioni:

Spiral and tap drills, broaching tools, engraving tools, ejectors, metal saws. 

Physical properties (avarage values) at ambient temperature

Modulu d'elasticità [103 x N/mm2]: 210 

Densità [g/cm3] : 7.80

Thermal conductivity [W/m.K]: 33.5, 32 (500°C), 31 (700°C)

Resistività elettrica [Ohm mm2/m]: 0.33

Capacità calori specifica [J/gK]: 0.46

Coefficient of Linear Thermal Expansion 10ˉ6 °C-1

20-100 ° C20-200 ° C20-300 ° C20-400 ° C20-500 ° C
11.812.512.913.513.7

Ricottura dolce:

Calore à 710-850 ° C, rinfriscà lentamente in furnace. Questu pruducerà una durezza Brinell massima di 223.

Stress Relief:

Stress relieving to remove machining stresses should be carried out by heating to approx. 650C, holding for 1-2 hours at heat, followed by air cooling. This operation is performed to reduce distortion during heat treatment.

Indurimentu:

Harden from a temperature of 780-820°C, 800-840°C followed by water or oil quenching. Hardness after quenching is 64-66, 64-66 HRC.

Temperatura:

Température de tempérament : 100-400°C.

Température de Température (°C) versus dureté (HRC)

100 ° C200 ° C300 ° C400 ° C450 ° C
6463595447

Forgiatura:

Temperature di furmazione à caldu: 1050-850 ° C. 

Usinabilità:

Nisun dati.

Corrosion Resistance :

This is an alloy steel and it is not corrosion resistant. It will rust unless protected.

ItemDimensione (mm)prucessuCundizione di consegna
Ronda BarDIA 1.0 - 30Disegnu à fretu / rettifica senza centruBright & Anneal
DIA 20 - 80sbucciaturaBright & Anneal
DIA 13-180Rolled HotSuperficie nera & Anneal
DIA 70 - 400Rolled HotSuperficie nera & Anneal
Pianu BarT 3.0-20 XW 20-100Rolled HotSuperficie nera & Anneal
BloccuT 20-200 X 300-800Laminato a caldo e forgiato a caldoSuperficie nera / Machine & Anneal
Rod RodDIA 5.5 - 13Rolled HotSuperficie nera & Anneal
FullesT1.0 - 2.5Ghjuvatu fridduSuperficie nera & Anneal
T 2.5 - 8.0Rolled HotSuperficie nera & Anneal