T1 1.3355 SKH2

Početna>Proizvodi>Brzi čelik>T1 1.3355 SKH2

HSS T1 1.3355 round bar

Kontaktiraj nas

Specifikacije

T1 čelik je alatni čelik tipa volfram. Vrlo visoka otpornost na habanje i omekšavanje. Dobra žilavost i sposobnost rezanja. Reakcija na duboko očvršćavanje.


Brza detalja:

T1 1.3355 ROUND BAR 

SASTAV

CSiMn
P&S
Cr
V
W
0.65-0.80
0.20-0.40
0.10-0.40
0.03max
3.75-4.50.90-1.30
17.25-18.75


Aplikacije:

O primjeni odlučuje kemijski sastav i svojstva čelika T1. 

Uglavnom se koristi za izradu složenih oštrica i alata za rezanje metala otpornih na udarce. 

Takođe može proizvoditi visokotemperaturne ležajeve i kalupe za hladno ekstruziju. 

Također se koristi za izradu zupčanika, alata za glodanje i alata kao što su bušilice, glodala itd.


Specifikacije:Round Bar

Specification: diameter: 12mm – 220mm; length: can be customized

Surface: Black Surface/Bright Surface/ Grinded/Peeled/Turned

       

RELATIVNA SVOJSTVA

tretman       temperature RangeCooling/Quenchingbilješke
kovanje1700-2100 ° FsporoCool slowly in dry sand or in other insulating media
prekaljivanje1600-1650 ° FCool slowly at a rate of 35° F per hour to 1000° FFor best results, insulating media is desirable. Hold at temperature for 2 hours
Smanjenje naprezanja1100-1300 ° FCool slowlyStress relieve after rough machining
Predgrevanje1500-1550 ° F
Preheat time in furnace is Hr. per inch of thickness. Heating up to temperature as slow as possible
Otvrdnjavanje2325-2375° F(furnace) 2275-2350°F(salt bath)Quench in air or warm oil. To minimize quenching strains, quench in salt at 1000° FFor maximum wear resistance, harden at 2375° F. For maximum toughness and high hardness, harden at 2275° F
Kaljenje1022° F-1058°FTemper T1 tool steel immediately after quenching. Hold for at least 2 hoursDouble tempering is recommended. The usual tempering time is 2+2 hours.Recommended temperature is 1000-1075° F for cutting tools. 1100-1200° F for shock tools


stavkaDimenzija (mm)procesUslov isporuke

Round Bar

DIA1.0 - 30Hladno crtanje / Brušenje bez centraBright & Anneal
DIA20 - 80PilingBright & Anneal
DIA 13-180Vruće valjanoCrna površina i žarenje
DIA 70 - 400Vruće valjanoCrna površina i žarenje