Cold Working Tool Steel O1 1.2510 SKS3 sheets

Kontaktiraj nas

Specifikacije

O1 tool steel is a low alloy cold work tool steel that must be oil-quenched in heat treatment. O1 tool steel contains small amounts of manganese, tungsten, and chromium, giving O1 tool steel adequate toughness for normal tool & die uses. O1 tool steel has deep hardening properties with fine grain structure with unusual toughness. O1 tool steel has good response to heat treatment with small dimensional changes. Sizes over approximately 2 inches thick or round may exhibit a lower hardness in the interior. O1 tool steel is available in standard de-carb free rounds, flats and squares, as well as the largest size selection in ground flat stock and drill rod of all the tool steel grades.


Aplikacije:

Tamo gdje je potrebna veća stabilnost dimenzija u toplinskoj obradi ili poboljšana otpornost na habanje, treba uzeti u obzir alatne čelike s većim sadržajem legure, kao što su A2 ili D2.


SASTAV

CMnSi
Cr
W
0.94
1.200.300.50
0.50


Specifikacije:

ASTM O1 Tool Steel Mechanical Properties

svojstvaMetričkiImperijalni
Hardness, Brinell (soft annealed -delivery condition)190190
Hardness, Rockwell C (tempering temp 300-1200°F)34.0-64.034.0-64.0
Elastic modulus (hardened to 62 HRC)193 GPa28000 ksi
Elastic modulus (@399°C/750°F, hardened to 62 HRC )172 GPa25000 ksi
Elastic modulus (@191°C/375°F, hardened to 62 HRC)186 GPa27000 ksi
Compressive yield strength (0.2%, hardened to 50 HRC)1350 MPa196000 psi
Compressive yield strength (0.2%, hardened to 55 HRC)1800 MPa261000 psi
Compressive yield strength (0.2%, hardened to 60 HRC)2150 MPa312000 psi
Compressive yield strength (0.2%, hardened to 62 HRC)2200 MPa319000 psi


Fizička svojstva

svojstvaMetričkiImperijalni
Density (hardened to 62 HRC)7.81 g / cm30.282 lb / inč3
Density (@399°C/ 750°F, hardened to 62 HRC)7.70 g / cm30.278 lb / inč3
Density (@191°C/ 375°F, hardened to 62 HRC)7.75 g / cm30.280 lb / inč3
Tačka topljenja1421 ° C2590 ° F


Toplinska svojstva

svojstvauslovi
T (° C)tretman
Toplinsko širenje10.6 x 10-6/ºC20-260-


Forging of ASTM O1 Tool Steel

Heating for forging of oil tool steel O1 must be done slowly and uniformly. Forging of alloy O1 steels can be performed at 980-1000°C, and reheat as often as necessary. But not forge below 800°C. After forging AISI O1 tool steel, cool slowly in lime, mica, dry ashes or furnace. ASTM O-1 tool steels should always be annealed after forging.


AISI O1 Tool Steel Heat Treatment


Anneal

Žarenje se mora izvesti nakon vruće obrade i prije ponovnog kaljenja.

Heat at a rate not exceeding 222°C per hour to 802-816°C, and hold at temperature for 1 hour per inch (25.4mm) of maximum thickness; 2 hours minimum. Then cool slowly with the furnace at a rate not exceeding 28°C per hourto 538°C. Continue cooling to ambient temperature in the furnace or in air. The resultant hardness should be a maximum of 212 HBW.


Stress Relief of Unhardened Material

Heat slowly to 1250° F. Soak for two hours per inch of thickness at heat. Slow cool (furnace cool if possible) to room temperature.


Hardening

1.Preheat: Warm slightly before charging into the preheat furnace, which should be operating at about 1100°-1200°F.

2.Hardening: Heat to 1475 to 1500° F. Soak at heat for 30 minutes per inch of thickness.

3.Quench: Quench O1 steel in warm oil and allow to cool in the oil until a temperature of 125°-150°F has been reached, or to where the part can be held in the bare hand, and temper immediately.

4.Temper: Normally oil hardening steels need to be single tempered only. However, double tempering may sometimes be preferred. Soak at heat for 2 hours per inch of thickness for each temper. Air cool to room temperature between tempers. The normal tempering range for this grade is 300 to 450° F.


 Stress Relief Temper

A stress relief temper for hardened material is strongly recommended after significant grinding, or welding, or EDM. Select a temperature that is 25 or 50° F lower than the last tempering temperature used.


 stavkaDimenzija (mm)procesUslov isporuke
listoviT1.0 - 2.5Hladno valjanaCrna površina i žarenje
T 2.5 - 8.0Vruće valjanoCrna površina i žarenje