M2 1.3343 SKH9

Početna>Proizvodi>Brzi čelik>M2 1.3343 SKH9

Okrugla šipka od brzog čelika

Kontaktiraj nas

Specifikacije

M2 High Speed Steel (M2) is a tungsten-molybdenum high speed steel with a well balanced composition suitable for a wide variety of applications.  World wide, the M2 type is by far the most popular high speed steel having replaced T1 high speed in most applications because of its superior properties and relative economy.

PRIJAVE:Twist drills, taps, milling cutters, reamers, broaches, saws, and knives.

SASTAV

C Mn Si Cr W Mo V
0.850.280.304.156.155.001.85


RELATIVNA SVOJSTVA

1492426826144581

Koeficijent toplinske ekspanzije (65-66 HRC)

Temperatura︒F

in/in︒F×10-6

Temperatura︒C

mm/mm︒C×10-6

70-200

5.69

21-93

10.23

70-400

6.09

21-204

10.95

70-600

6.42

21-316

11.55

70-800

6.67

21-427

12

70-1000

6.97

21-358

12.54

FIZIČKE SVOJINE

· Gustina: 0.294 lb/in3 (8138 kg/m3)

· Specifična težina: 8.14

· Modul elastičnosti: 30 x 106 psi (207GPa)

· Obradivost: 50-60% 1% ugljeničnog čelika


1492427347894659


UPUTSTVO ZA TOPLINSKU OBRADU

KALJIVANJE

KRITIČNA TEMPERATURA:

Ac1: 1530°F (832 ℃)

Ac3: 1610°F (877 ℃)

AR1: 1430°F (777 ℃)

AR3: 1380°F (749 ℃)

Predgrevanje: To minimize distortion and stresses in large or complex tools use a double preheat. Heat at a rate not exceeding 400°F per hour (222°C per hour) to 1100°F (593°C) equalize, then heat to 1450-1550°F (788-843°C). For normal tools, use only the second temperature range as a single preheating treatment.

Austenitizacija (visoka toplota): Brzo zagrijte od prethodnog zagrijavanja.
For Cutting Tools:
Peć: 2200-2250°F (1204-1232°C)
Sol: 2175-2225°F (1191-1218°C)
Za maksimalnu žilavost koristite najnižu temperaturu.
Za maksimalnu tvrdoću na vrućini koristite najvišu temperaturu.
For punches, dies, and tools that require maximum
toughness without hot hardness:
Peć: 2075-2175°F (1175-1191°C)
Sol: 2050-2150°F (1121-1177°C)

Gašenje: Pressurized gas, warm oil, or salt. For pressurized gas, a rapid quench rate to below 1000°F (538°C) is critical to obtain the desired properties. For oil, quench until black, about 900°F (482°C), then cool in still air to 150 -125°F (66-51°C). For salt maintained at 1000-1100°F (538-593°C), equalize, then cool in still air to 150 -125°F (66-51°C).

Kaljenje: Kaljenje odmah nakon gašenja. Tipični raspon temperiranja je 1025-1050°F (552-566°C). Držite na temperaturi 2 sata, a zatim ohladite na temperaturi okoline. Potrebno je dvostruko kaljenje. Za velike poprečne presjeke, a posebno za zareze iz kojih će se alati rezati žicom EDM, trostruko kaljenje se preporučuje.

ANNEALING

Žarenje se mora izvesti nakon vruće obrade i prije ponovnog kaljenja.

Heat at a rate not exceeding 400°F per hour (222°C per hour) to 1525-1550°F (829-843°C), and hold at temperature for 1 hour per inch (25.4 mm) of thickness, 2 hours minimum. Then cool slowly with the furnace at a rate not exceeding 50°F per hour (28°C per hour) to 1000°F (538°C). Continue cooling to ambient temperature in the furnace or in air. The resultant hardness should be 248 HBW or lower.


stavkaDimenzija (mm)procesUslov isporuke
Round BarDIA1.0 - 30Hladno crtanje / Brušenje bez centraBright & Anneal
DIA20 - 80PilingBright & Anneal
DIA 13-180Vruće valjanoCrna površina i žarenje
DIA 70 - 400Vruće valjanoCrna površina i žarenje
Ravna šipkaT 3.0-20 XW 20-100Vruće valjanoCrna površina i žarenje
BlokT 20-200 X 300-800Vruće valjani i vruće kovaniCrna površina / mašina i žarenje
Žičani štapDIA 5.5 - 13Vruće valjanoCrna površina i žarenje
listoviT1.0 - 2.5Hladno valjanaCrna površina i žarenje
T 2.5 - 8.0Vruće valjanoCrna površina i žarenje