D2 1.2379 SKD11 flat bar

Kontaktiraj nas

Specifikacije
D2 Tool Steel is a versatile high-carbon, high-chromium, air-hardening tool steel that is characterized by a relatively high attainable hardness and numerous, large, chromium-rich alloy carbides in the microstructure. These carbides provide good resistance to wear from sliding contact with other metals and abrasive materials. Although other steels with improved toughness or improved wear resistance are available, D2 provides an effective combination of wear resistance and toughness, tool performance, price, and a wide variety of product forms. Also available as an Electro-Slag-Remelted (ESR) product. The remelting process provides improved chemical homogeneity, refinement of carbide size, and the associated improvements in mechanical and fatigue properties.

PRIJAVE: Valjci, bušilice, matrice za izrezivanje, oblikovanje, obrezivanje i valjanje navoja, noževi za smicanje, noževi za preradu hrane i mjerači.

SASTAV

C

Mn

Si

Cr

Mo

V

1.50

0.30

0.30

12.00

0.75

0.90


RELATIVNA SVOJSTVA

1492431879960282

Koeficijent toplinske ekspanzije (58-59 HRC)

Temperatura︒F

in/in︒F×10-6

Temperatura︒C

mm/mm︒C×10-6

100-500

5.71

38-260

10.3

100-800

6.63

38-427

11.9

100-1000

6.82

38-538

12.3

100-1200

6.83

38-649

12.3

100-1500

6.9

38-816

12.4

FIZIČKE SVOJINE

· Gustina: 0.278 lb/in3 (7695 kg/m3)

· Specifična težina: 7.70

· Modul elastičnosti: 30 x 106 psi (207GPa)

· Obradivost: 50-60% 1% ugljeničnog čelika

1492431918971275

UPUTSTVO ZA TOPLINSKU OBRADU

KALJIVANJE

KRITIČNA TEMPERATURA:

Ac1: 1449°F (788 ℃)

Ac3: 1553°F (845 ℃)

AR1: 1418°F (769 ℃)

AR3: 1373°F (744 ℃)

Predgrevanje: To minimize distortion and stresses in large or complex tools use a double preheat. Heat at a rate not exceeding 400°F per hour (222°C per hour) to 1150-1250°F (621-677°C) equalize, then heat to 1400-1450°F (760-788°C). For normal tools, use only the second temperature range as a single preheating treatment.

Austenitizacija (visoka toplota): Polako zagrijte od prethodnog zagrijavanja. Peć ili so: 1850-1875°F (1010-1024°C).

Quenching: Air or pressurized gas to 150-125ºF (66-51ºC). Sizes up to 4 inches (101.6 mm) in thickness will through harden when air cooled from 1575ºF (857ºC). Sizes up to 6 inches (152.4 mm) in thickness will through harden when air cooled from 1625ºF (885ºC).

Kaljenje: Kaljenje odmah nakon gašenja. Držite na temperaturi 1 sat po inču (25.4 mm) debljine, najmanje 2 sata, a zatim ohladite na zraku do temperature okoline. Tipični raspon temperiranja je 350 do 400ºF (177 do 204ºC).

Za maksimalnu otpornost na habanje, temperirajte između 300-350°F (149-177°C) za tvrdoću od 62-64 HRC. Za optimalnu ravnotežu između otpornosti na habanje i žilavosti, kaljenje između 500-550°F (260-288°C). Ovo će proizvesti 58-60 HRC.

Za maksimalnu žilavost, dvostruko kaljenje, 2 sata plus 2 sata, na temperaturama iznad 950°F (510°C). Ovo će proizvesti tvrdoću manju od 58 HRC.

To minimize internal stresses in cross sections greater than 6 inches (152.4 mm) and to improve stability in tools that will be EDM'd after heat treatment, soaking times of 4 to 6 hours at the tempering temperature below 950°F (510°C) are strongly recommended.

Annealing: Žarenje se mora izvesti nakon vruće obrade i prije ponovnog kaljenja. Zagrijati brzinom koja ne prelazi 400°F na sat (222°C na sat) do 1600-1650°F (871-899°C), i držati na temperaturi 1 sat po inču (25.4 mm) maksimalne debljine; 2 sata minimum. Zatim polako ohladite u peći brzinom koja ne prelazi 50°F na sat (28°C na sat) do 1000°F (538°C). Nastavite sa hlađenjem na temperaturu okoline u peći ili na zraku. Rezultirajuća tvrdoća bi trebala biti maksimalno 255 HBW.

stavkaDimenzija (mm)procesUslov isporuke
Round BarDIA1.0 - 30Hladno crtanje / Brušenje bez centraBright & Anneal
DIA20 - 80PilingBright & Anneal
DIA 13-180Vruće valjanoCrna površina i žarenje
DIA 70 - 400Vruće valjanoCrna površina i žarenje
Ravna šipkaT 3.0-20 XW 20-100Vruće valjanoCrna površina i žarenje
BlokT 20-200 X 300-800Vruće valjani i vruće kovaniCrna površina / mašina i žarenje
Žičani štapDIA 5.5 - 13Vruće valjanoCrna površina i žarenje
listoviT1.0 - 2.5Hladno valjanaCrna površina i žarenje
T 2.5 - 8.0Vruće valjanoCrna površina i žarenje