M1 Bright bar tanıtımı

Saat: 2023-07-07 Oxunub: 12

Standartlar üzrə təyinat

Marka adıMat. Yox.DINENAISI
KSD-M11.3346S2-9-1-M1

Kimyəvi Tərkibi (çəki %)

CSiMnCrMoNiVWqeyriləri
0.82maksimum 0.45maksimum 0.403.858.60-1.151.75-

təsvir
M1 is a molybdenum, chromium, vanadium alloy tool steel generally known as a Molybdenum High Speed Tool Steel. It is on of the most widely available tool steels in use today. It is similar in properties to the tungsten tool steels (T series) at a lower. Very tough high-speed Mo steel good grindability.

Applications
Twist drills, thread cutting tools, hobs and dies for broaching and cold flow pressing, cross recess dies for screw manufacture, cold rolling for e.g. Sendzimir equipment.
Ətraf mühitin temperaturunda fiziki xüsusiyyətlər (orta qiymətlər).
Modulus of elasticity [103 x N/mm2]: 217
Sıxlıq [q/sm3]: 8.0
İstilik keçiriciliyi [W/mK]: 19.0
Elektrik müqaviməti [Ohm mm2/m]: 0.60
Xüsusi istilik tutumu[J/gK]: 0.46

Coefficient of Linear Thermal Expansion 10-6 oC-1

20-100oC20-200oC20-300oC20-400oC20-500oC20-600oC20-700oC
11.011.511.912.312.412.512.5

Yumşaq tavlama
Heat to 820-850oC, cool slowly in furnace to 550oC then air. This will produce a maximum Brinell hardness of 262.

Stress Relieving
Stress relieving to remove machining stresses should be carried out by heating to 600-650oC, holding for one hour at heat, followed by air cooling. This operation is performed to reduce distortion during heat treatment.

Sərtləşmə
0 Harden from a temperature of 1180-1219oC followed by air or oil quenching or warm bath at 550oC. Hardness after quenching is 64-66 HRC.

Tempering
Tempering temperature: 530 – 560oC, at least 2x for at least 63 HRC.

Döymə
Hot forming temperature: 1100-900oC.

Soyuq işləmə
This alloy may be cold worked in the annealed condition.

Dəzgah
M1 is classified as a “medium” machinable alloy. Machining should be accomplished prior to hardening heat treatment followed by finish grinding. It has a rating of 50% that of the water hardening (W group) low alloy tool steels in regard to machinability.

Korroziyaya davamlılığa
This is not a corrosion resistant alloy. In use as tooling it is often coated with oil to prevent rusting. A light film of oil. or protective wrapping, is essential to keep it free from corrosion.

Qaynaq
Consult the alloy supplier for information on weld procedures.